- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 207 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 207 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
ASTM D 648 |
| SABIC Innovative Plastics Cycolac® INP562 ABS SABIC INP562 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics Cycolac® INP562 ABS+SAN SABIC INP562 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pellet.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® MG38 ABS (Asia Pacific) Very high impact ABS. Toughness/rigidity. Good fatigue resistance. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® MG38F ABS Very high impact ABS. Toughness/rigidity. FDA compliant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycolac® X11 ABS Automotive: High heat resistance. Excellent flow/impact balance. UL94 HB rated. High gloss. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Cycoloy® CE3210 PC+ABS (Europe-Africa-Middle East) Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 °C | 207 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylac® GP55 ABS Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Rava.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | Unannealed; ASTM D648 |
| Phillips 66 COPYLENE® CM120LN Polypropylene Impact Copolymer COPYLENE™ CM120LN is a high impact copolymer formulated with antistat and nucleated for demanding injection molding applications.Applications: Injection molding applications including crates, totes.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Geloy FXTW26SK ASA (Europe-Africa-Middle East) Next generation Geloy XTW ASA for high heat exterior applications. Outstanding weatherability and toughness. Metallic sparkle VisualFx.This data was supplied by SABIC-IP for the Europe-Africa-Middle.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | |
| Ineos ABS Lustran® QE 1094 AS, Injection Grade
(discontinued **) Injection molding grade, super high impact.Information provided by Bayer.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 °C | 207 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylac® EX28 ABS Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Rava.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ASTM D648 |
| Flint Hills AP5325-HS Impact Copolymer Polypropylene High impact copolymer, UL certified, and FDA compliant. Features: Nucleated and heat stabilizedApplications: Injection molding: large, thin wall automotive interior parts.Former Huntsman polypropyle.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa H-12 Modified ABS Features:UL94 HB @ 1.6-3.0mmHigh toughnessHeat resistanceApplications:Automobile exterior trimAutomobile interior trimPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ISO 75-1,-2 |
| Ineos ABS Lustran® ABS 240 Injection Molding Grade Lustran® ABS 240 has standard impact strength and is injection molding grade. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 °C | 207 °F | ASTM D648 |
| Ineos H19G-01 Polypropylene Homopolymer Grade H19G-01 is a polypropylene homopolymers designed for extrusion processing and meet the requirements of the U.S. Food and Drug administration as specified in 12 CFR 177.1520.Applications:Contin.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ISO 75-1,-2 |
| Inno-Comp INNOPOL® CS 2-9524 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer INNOPOL® CS 2-9524 is a 20% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-9524 is dev.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon NX03602 PC+ABS LNP STAT-KON* NX03602 is a compound based on PC+ABS Blend resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP CX05470 PS LNP* THERMOCOMP* CX05470 is a compound based on Polystyrene resin containing 20% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP CX05470 PS LNP* THERMOCOMP* CX05470 is a compound based on Polystyrene resin containing 20% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOTUF CF007IXP PS LNP* Thermotuf* CF007IXP is a compound based on Polystyrene containing glass fiber. Characteristics of this grade are: High Impact. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ASTM D648 |
| Formosa Plastics Formolene® 2575N injection Molded Polypropylene Impact Copolymer for High Speed injection Molded ApplicationsFormolene® 2575N is a very high melt flow, medium impact copolymer of polypropylene. It is designed for such applications as packaging, .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ISO 75-2 |
| Borealis Daplen™ EE260AE Scratch Resistant Polypropylene Compound Daplen EE206AE is a 20% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE206AE is optimized to provide excellent scratch resistance on gained and unpai.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | Annealed; ISO 75-2A |
| Total PSC 1160/1160N Crystal Polystyrene 1160 is a high resistance, high molecular weight crystal polystyrene mainly for the extrusion industry. Most notable for the production of bi-oriented polystyrene (BOPS). It is particularly useful.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ASTM D648 |
| Formosa Plastics Formolene® 6613N Impact Copolymer Polypropylene Copolymer for Injection Molded Applications Requiring a Combination of High Toughness and Stiffness Formolene® 6613N is a copolymer of polypropylene designed and formulated for injection molding ap.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 °C | 207 °F | ISO 75-2/B |
| ExxonMobil Exxtral™ BMU 234 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive exterior parts and high stiffness, high impact and good dimensional stability.Availability: Africa & Middle Ea.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ASTM-D648 |
| Braskem H 503HS HOMO Polypropylene Homopolymer H 503HS is a low melt flow rate homopolymer for general purpose. It is designed for raffia extrusion and fiber extrusion. This product exhibits excellent processability, high speed production with g.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ASTM-D648 |
| Braskem PD 943XP HOMO Polypropylene Homopolymer PD 943XP is a medium melt flow rate homopolymer with slip and antiblocking agents. It is suitable for blown film extrusion. This product features good impact strength, excellent gloss and transparen.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.2 °C | 207 °F | ASTM D648 |
| Americas Styrenics EA3130 High Heat Crystal Polystyrene Product CharacteristicsAdditive FreeFood Contact CompliantTypical ApplicationsMedical PartsColor Concentrate CarrierLow Profile AdditivesInformation provided by AmericasStyrenics LLC. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | Annealed, 80°C, 4 hours; ISO 75 |
| LG Chemical HF-380 ABS, High Flow, High Impact Feature: Injection Molding, High FlowApplication: Electric & Electronic Products, Toys, Miscellaneous Goods)CAS No. 9003-56-9Information Provided by LG Chem |
|||