SABIC Innovative Plastics Cycolac® INP562 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® INP562 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SABIC INP562 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pelletized and dry blend concentrate; provides a base resin with less heat history than pellets; suitable for direct weather exposure; can be used in all SAN applications where a fine particle size is desired.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D 792
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Melt Flow 6.4 g/10 min

@Load 3.80 kg,
Temperature 230 °C
6.4 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D 1238
16 g/10 min

@Load 10.0 kg,
Temperature 220 °C
16 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D 785
Tensile Strength at Break 74.0 MPa
10700 psi
Type I, 5 mm/min; ASTM D 638
78.0 MPa
11300 psi
50 mm/min; ISO 527
Tensile Strength, Yield 74.0 MPa
10700 psi
Type I, 5 mm/min; ASTM D 638
78.0 MPa
11300 psi
50 mm/min; ISO 527
Elongation at Break 2.2 %
2.2 %
50 mm/min; ISO 527
2.9 %
2.9 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 2.2 %
2.2 %
50 mm/min; ISO 527
2.9 %
2.9 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 3.83 GPa
555 ksi
5 mm/min; ASTM D 638
3.95 GPa
573 ksi
1 mm/min; ISO 527
Flexural Yield Strength 74.0 MPa
10700 psi
2 mm/min; ISO 178
103 MPa
14900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 3.46 GPa
502 ksi
2 mm/min; ISO 178
3.78 GPa
548 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.220 J/cm

@Temperature 23.0 °C
0.412 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
0.230 J/cm

@Temperature -30.0 °C
0.431 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
Izod Impact, Notched (ISO) 2.00 kJ/m²

@Temperature 23.0 °C
0.952 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
2.00 kJ/m²

@Temperature -30.0 °C
0.952 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.100 J/cm²

@Temperature 23.0 °C
0.476 ft-lb/in²

@Temperature 73.4 °F
ISO 179/2C
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 97.0 °C

@Thickness 3.20 mm
207 °F

@Thickness 0.126 in
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
84.0 °C

@Thickness 3.20 mm
183 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 104 °C
219 °F
Rate B/50; ISO 306
106 °C
223 °F
Rate B/120; ISO 306