Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 309 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 3.18 mm |
309 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ NT-818.B001-7001 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 3.18 mm |
309 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ NT-818.B001-8000 Polypropylene, Unspecified (PP, Unspecified) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® 3414R PC (Asia Pacific) 40% GR, provides improved mechanical properties and UL94V-1 rated at 0.058"". Internal mold release added. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylex® P1010G40 HB Polycarbonate, 40% Fiberglass Reinforced Information provided by Ravago. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| Custom Resins Vexel™ 3250 PBT
(discontinued **) General Purpose Unreinforced; High Flow. Property data for dry as molded samples.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical Lupox® GP1000H PBT Description: Injection Molding, PBT, High Flow, High ImpactApplication: Automotive (Connector)CAS No. 155123-66-3 and 24968-12-5Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical Lupox® GP1000M PBT Description: Injection Molding, PBT, High Flow, High ImpactApplication: Automotive (Connector)CAS No. 155123-66-3 and 24968-12-5Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| LG Chemical Lupox® HV-1010 General Purpose PBT, Unreinforced, High Viscosity LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| LG Chemical Lupox® SV-1080 General Purpose PBT, Unreinforced, High Molecular Weight, Extrusion LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP RP004S PA 66 LNP* LUBRICOMP* RP004S is a compound based on Nylon 66 containing PTFE/Silicone. Added features of this grade include: Heat Stabilized, Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Valox® 295 PBT Unreinforced PBTThis data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Valox® 312 PBT Unreinforced, For compounding only (not for injection molding), FDA (21 CFR 177.1660) compliant. Medium viscosity.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 325 PBT General purpose, unreinforced, improved processing. Applications like sprinklers and nozzles, pumps, door handle, tank covers, pens, pencils etc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP MFB63 PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MFB63 is a compound based on Polypropylene resin containing Glass Bead, Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66 Noryl GTX* GTX942 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is designed to have high melt flow for large part/thinwall injection molding. The material is designed to h.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PX1390 PPE+PS Automotive applications, primarily. Excellent electrical properties, easy processability, high heat, 295F (146C) DTUL. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 3.20 mm |
309 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP MF002S PP LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ISO 75-2 |
| Borealis GB205U Polypropylene Compound, Glass Fiber Reinforced GB205U is a 20% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. The product is available in natural but other colors can be provided on request. Thi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer DescriptionPolyfort® FPP 3459 is a 30% glass filled copolymerInformation provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer DescriptionPolyfort® FPP 3459 is a 30% glass filled copolymerInformation provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ISO 75 |
| Polyram RamOfin PPH343T4BK10 Polypropylene, 20% Mineral Filled 20% Mineral filled, heat resistant polypropylene for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer DescriptionPolyfort® FPP 3459 is a 30% glass filled copolymerInformation provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3460 Glass-Mineral Hybrid Filled Copolymer DescriptionPolyfort® FPP 3460 is a 40% glass-mineral hybrid filled copolymer.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| Entec Hypro™ PPH-GF30 Natural Homopolymer Polypropylene, 30% Glass Reinforced Information provided by Entec |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0336G20M10CL Glass/Mineral Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 103 Polypropylene, Glass Reinforced, Chemically Coupled, Impact Modified Data provided by the manufacturer, ComAlloy International Company.15% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| A. Schulman ComAlloy Comtuf® 420 Polyester - PBT, High Impact Modified Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| Adell RR-16 Copolymer Polypropylene, 30% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3459 Glass Filled Impact Copolymer DescriptionPolyfort® FPP 3459 is a 30% glass filled copolymerInformation provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ISO 75 |
| Manifattura Cattaneo POM c+PTFE Acetal, PTFE Filled Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a. |
|||