- SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66
SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl GTX* GTX942 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is designed to have high melt flow for large part/thinwall injection molding. The material is designed to have the excellent chemical resistance and paintability as other Noryl GTX Resins.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.520 % | 0.520 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.01 % | 1.01 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0113 - 0.0126 cm/cm @Thickness 3.20 mm |
0.0113 - 0.0126 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 18.5 g/10 min @Load 5.00 kg, Temperature 280 °C |
18.5 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 280 °C |
17 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | Type I, 50 mm/min; ASTM D638 |
| 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
| 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 43.9 % | 43.9 % | Type I, 50 mm/min; ASTM D638 |
| 58.2 % | 58.2 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.6 % | 4.6 % | Type I, 50 mm/min; ASTM D638 |
| 7.1 % | 7.1 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.44 GPa | 354 ksi | 5 mm/min; ASTM D638 |
| 2.58 GPa | 374 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 87.0 MPa | 12600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.22 GPa | 322 ksi | 2 mm/min; ISO 178 |
| 2.26 GPa | 328 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.65 J/cm | 4.96 ft-lb/in | ASTM D256 |
| 1.17 J/cm @Temperature -30.0 °C |
2.19 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1A |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.30 J/cm² | 10.9 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 46.0 J @Temperature 23.0 °C |
33.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 100 µm/m-°C @Temperature 23.0 - 80.0 °C |
55.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
27.8 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 160 °C @Thickness 3.20 mm |
320 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 169 °C | 336 °F | Rate B/50; ISO 306 |
| 169 °C | 336 °F | Rate B/120; ISO 306 | |
| 171 °C | 340 °F | Rate B/50; ASTM D1525 |