- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 60.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 60.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | Compression Molded; ASTM D648 |
| NOVA Chemicals Surpass® RMs539-UG Octene sMDPE Rotational Molding Film Features: Octene copolymerExceptional low temperature impact propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Stan.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 98.9 °C | 140 - 210 °F | Average value: 70.6 °C Grade Count:10 |
| Overview of materials for PETG Copolyester This property data is a summary of similar materials in the MatWeb database for the category "PETG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D1525 |
| NOVA Chemicals Novapol® TR-0535-U Hexene MDPE Rotational Molding Resin
(discontinued **) Molded Plaque Properties. Features: Hexene Copolymer, excellent impact strength, excellent ESCR.Applications: large parts, agricultural storage tanks.Data provided by the manufacturer. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| LyondellBasell Alathon® M4621 High Density Polyethylene ApplicationsALATHON M 4621 is a copolymer that provides outstanding stress crack resistance and low temperature impact strength. Typical applications include small two-piece engine gas tanks, waste.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| LyondellBasell Alathon® M4661 High Density Polyethylene ApplicationsALATHON M 4661, formerly known as LYHD 060, exhibits excellent impact, warp and environmental stress crack resistance. Typical applications are closures, institutional seating and consum.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Lubrizol Stat-Rite® M-690 Static Control PETG Alloy Stat-Rite® M-690 is a static dissipative PETG alloy. Stat-Rite® M-690 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protectio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ISO 75-2 |
| Borealis Bormed™ RB801CF Polypropylene Random Copolymer Bormed™ RB801CF is a random copolymer. Applications: Bormed™ RB801CF is intended for packaging for medical devices, pouches, and packaging for pharmaceutical products. Additives: Bormed™ RB801C.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Lubrizol Stat-Rite® S-680 Static Control PETG Alloy Stat-Rite® S-680 is a static dissipative PETG alloy. Stat-Rite® M-680 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to provide clean, permanent ESD protectio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | |
| Covestro Texin® 260 Urethane Thermoplastic Elastomer Key Features:UnfilledSuitable processing methods:Injection moldingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adop.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Dow DOWLEX™ IP-51 High Density Polyethylene Resin (HDPE) DOWLEX™ IP-51 is an Improved Processing high density resin designed to offer excellent process-ability and impact performance. This resin was designed by optimization of the breadth, shape and pea.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ISO R75 |
| Arkema Group Orgalloy® LT 4060 Polyamide Alloy Polyamide Alloy, Flexible gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM-D648 |
| Braskem ML3601U LLDPE Rotomolding Polyethylene The resin ML3601U is a linear low-density polyethylene, 1-hexene based, with excellent environmental stress cracking resistance and high impact strength. It contains long term UV8 stabilization and .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM-D648 |
| Braskem ML4400N LLDPE Rotomolding Polyethylene The resin ML4400N is a linear low-density polyethylene, 1-butene based, with high stiffness and an adequate balance of processability and environmental stress cracking resistance. It contains long t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 65.0 °C | 140 - 149 °F | |
| C.O.I.M. EXTER S® S 102 Orthophthalic Resin Description: The Exter S product line contains a large number of unsaturated polyester resin products with an array of properties and applications.Specific Notes for ESTER S® S 102: Resin suitable .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | |
| BASF Novolen® 3340 PC Polypropylene Nucleated grade for injection moldings with higher transparency.Data was collected by ISO methods and provided by BASF. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 75.0 °C | 140 - 167 °F | ASTM D648 |
| Arkema Group KYNAR FLEX® 2850 Black Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating, pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 75.0 °C | 140 - 167 °F | ASTM D648 |
| Arkema Group KYNAR FLEX® 2850-02 Polyvinylidene Fluoride Copolymer - Extrusion Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 75.0 °C | 140 - 167 °F | ASTM D648 |
| Arkema Group KYNAR FLEX® 2900-04 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible, flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C @Thickness 6.40 mm |
140 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical KEYFLEX BT S5035 Ester Type TPE Description: Injection Molding, TPC-ET, Airbag Cover Deployment, Medium Modulus, Black ColorApplication: Airbag Cover (DAB, PAB, KAB, SAB)CAS: 37282-12-5, 24968-12-5 and 1333-86-4Information provide.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Solvay TECHNYL® 1011R PA6, DRY Description: Polyamide 6, Unfilled, lubricated, for injection molding. Available in: Asia Pacific Product Applications: TECHNYL® 1011R is used in all sectors of industry, offering an excellent flow.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Solvay TECHNYL® 1015CR PA6, DRY Description: Polyamide 6, unfilled, standard for fast injection cycles, for injection molding Available in: Asia Pacific Product Applications: TECHNYL® 1015CR has high fluidity and a good mould re.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene DescriptionPolyfort® FXP 1943 is a 20% CAC03 and glass fiber hybrid copolymer polypropylene product. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 75.0 °C | 140 - 167 °F | ASTM D648 |
| Arkema Group KYNAR FLEX® 2800-20 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 75.0 °C | 140 - 167 °F | ASTM D648 |
| Arkema Group KYNAR FLEX® 2850-07 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |
|||