Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 83.9 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C @Thickness 3.18 mm	183 °F @Thickness 0.125 in	Annealed; ASTM D648
PolyOne Geon™ Vinyl Packaging 4195 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman...
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman...
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman...
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman...
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman...
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
A. Schulman PP 1498-01 Polypropylene Medium Impact Copolymer Polypropylene DescriptionPolypropylene PP 1498-01 is a high flow, medium impact copolymer polypropylene. It molds easily at low temperatures, pressures and mold cycle times. Information provided by A. Schulman...
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
CPC - Vycom SEABOARD™ Supreme DS High density polyethylene (HDPE) Seaboard DS is a high density polyethylene (HDPE) foam core product with a specially formulated skin to add stiffness and Dimensional Stability. This new product from Compression Polymers combines l..
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
ExxonMobil PP5341E1 Polypropylene Homopolymer Product Description: A low melt flow rate that provides high melt strength and resistance to softening at elevated temperature.Availability: North America Features:Low FlowUses: Automotive Applic..
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	Unannealed; ASTM D648
Dow 6D20 Polypropylene Random Copolymer Resin OverviewConsistent processabilityGood regrind stabilityGood gloss and clarityLow odor and taste transferComplies with: U.S. FDA 21 CFR 177.1520 (c)3.1a, Europe EU-Directive 2002/72/ECDOW 6D20 Polypr..
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	unannealed; molded and tested in accordance with ASTM D 4101; ASTM D648
Dow 6D20 Polypropylene Resin DOW 6D20 is intended for use in film and extrusion blow molding processes. It is especially suited for multilayered, barrier bottles.Information provided by DowDow Announced Sale of Global Polyprop..
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	Molded and tested in accordance with ASTM D4976; ASTM D648
Dow DMDA-8007 NT 7 High Density Polyethylene Resin DOW DMDA-8007 NT is a narrow molecular weight distribution high density homopolymer designed to offer excellent stiffness, low warpage, good/acceptable toughness, and good mold-ability. This resin ..
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	Unannealed; ASTM D648
Dow R131-02A Polypropylene Random Copolymer Resin DOW R131-02A Polypropylene Resin is a random copolymer intended for use in extrusion blow molding applications. The product can be used in both single layer and multilayer designs including barrier..
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	Unannealed; ASTM D648
Dow R132-02A Polypropylene Random Copolymer Resin DOW R132-02A Polypropylene Resin is a random copolymer intended for use in extrusion blow molding applications. The product can be used in both single layer and multilayer designs including barrier..
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
Aclo Accucomp ABS ABS801L Medium Impact Grade
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
Aclo Accucomp ABS ABS811L Medium Impact Grade
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
Americas Styrenics STYRON A-TECH® 1260 High Impact Polystyrene Product CharacteristicsGood Environmental Stress Crack Resistance (ESCR)Good practical toughnessDeep draw thermoforming capableGood low temperature impactFood Contact CompliantTypical ApplicationsPa..
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648
Aclo Accucomp ABS ABS804L High Impact Grade
Deflection Temperature at 0.46 MPa (66 psi)	83.9 °C	183 °F	ASTM D648B
Braskem TI6120AN High Impact Copolymer Polypropylene Description: Excellent balance of toughness and stiffness, unique dimensional stability and excellent flow properties.Applications: Suggested uses include compounding, injection molding, automotive ..