Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 8.0 MPa | 70.0 - 120 °C | 158 - 248 °F | Injection; ISO 75-C |
Raschig Group RALUPOL® 2200 UP Polyester Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets.. |
|||
Deflection Temperature at 8.0 MPa | 70.0 - 130 °C | 158 - 266 °F | Injection; ISO 75-C |
Raschig Group RALUPOL® 8601 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic moulding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical stren.. |
|||
Deflection Temperature at 8.0 MPa | 70.0 - 130 °C | 158 - 266 °F | Injection; ISO 75-C |
Raschig Group RALUPOL® 8602 UP Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical streng.. |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1,-2 |
Lanxess Durethan® AKV 15 H3.0 000000 Nylon 66, 15% Glass Fibers PA 66, 15% glass fibers, injection molding, heat-ageing stabilized |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
Lanxess Pocan® B 4215 000000 PBT, 12% Glass Fiber PBT, 12% glass fibers, injection molding, flame retardant |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
Lanxess Pocan® KU 2-7209 Z 000000 PBT, 15% Glass Fiber PBT, 15% glass fibers, injection molding, flame retardant, impact modified |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
Lanxess Durethan® AKV 15 000000 Nylon 66, 15% Glass Fiber PA 66, injection molding grade, 15% glass fibers |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
Lanxess Durethan® AKV 15 H2.0 901510 Nylon 66, 15% Glass Fiber PA 66, injection molding grade, 15% glass fibers, good heat-ageing resistance |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
Lanxess Pocan® BF 8230 000000 PBT, 30% Glass Fiber PBT, 30% glass spheres/glass fibers, injection molding, flame retardant, low tendency to warp, improved surface finish |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® AG-30 LF 15 PA66-(GF+Z)45 Product description: Grilon AG-30 LF 15 black 9832 is a heat stabilized, normal viscosity PA66 injection molding grade with 30% glass fibers and 15% of a combination of PTFE and silicone. Grilon AG-.. |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® BG-25 HM PA6-GF25 Product description: Grilon BG-25 HM is a heat stabilized, normal viscosity, and adhesion modified PA6 injection molding grade with 25% glass fibers. Grilon BG-25 HM has the following important prop.. |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® GVN-35H black 9915 PA*-GF35 Product description: Grivory GVN-35H is a 35% glass-fiber reinforced, impact-modified engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic c.. |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® TSG-30/4 LF 15 PA666-(GF+Z)45 Product description: Grilon TSG-30/4 LF 15 natural is a normal viscosity, heat stabilized PA 66 + PA 6- molding type with 30% glass fibre reinforcement and 15% of a combination PTFE and siliconoil. .. |
|||
Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® TSM-30 PA666-MD30 Product description: Grilon TSM-30 is a heat stabilized, normal viscosity PA66 + PA6 injection molding grade with 30% mineral. Grilon TSM-30 has the following important properties: Excellent surface.. |