- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 117 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 117 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | ISO 75/Method Af |
| Premix Thermoplastics PRE-ELEC® PBT 1455 PRE-ELEC PBT 1455 is a conductive thermoplastic compound based on PBT. Conductivity is achieved by using special conductive carbon black. PRE-ELEC PBT 1455 has excellent mechanical properties as wel.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | ASTM D648 |
| DuPont Performance Polymers Crastin® ST820 BK503 PBT
(Unverified Data**) Crastin® ST820 BK503 is an unreinforced, Super Tough, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 - 190 °C | 117 - 374 °F | Average value: 75.5 °C Grade Count:26 |
| Overview of materials for Nylon 612, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Unreinforced". Each property range of values reported is minimum and maximum values of approp.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | ASTM D648 |
| Garland Manufacturing GAR-DUR® Ultra High Molecular Weight Polyethylene (UHMW-PE) GAR-DUR® plastic parts are made from ultra high molecular weight (UHMW) polymer having a molecular weight of 4.2 million and greater. Garland Manufacturing Company has been processing UHMW resin .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 °C | 117 °F | Unannealed; ISO 75A-1, -2 |
| LyondellBasell Hifaxâ„¢ CA244 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CA244 high melt flow, 850 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has an excellent combination of stiffness, processability and dynamic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 °C | 117 °F | Unannealed; ISO 75A-1, -2 |
| LyondellBasell Hifaxâ„¢ CB251 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CB251 medium melt flow, 1,200 MPa flexural modulus, low CLTE, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of impact resis.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 °C | 117 °F | Unannealed; ISO 75A-1, -2 |
| LyondellBasell Hifaxâ„¢ Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CB252 medium high melt flow, 1,200 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has very well balanced processability, rigidi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP FL004 PE (Europe-Africa-Middle East) LNP* Lubricomp* FL004 is a compound based on Polyethylene resin containing PTFE. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP SP003 PA12 (Europe-Africa-Middle East) LNP* LUBRICOMP* SP003 is a compound based on PA 12 resin containing PTFE/Silicone. Added features include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C @Thickness 6.40 mm |
117 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 337 PBT Low temperature impact PBT. Automotive applications: underhood power distribution boxes and covers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Valox® V2105U PBT Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C @Thickness 3.20 mm |
117 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics Xenoy® X6800BM PBT Blow moldable, impact modifed XENOYThis data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP HB006 PA 11 (Asia Pacific) LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing Glass Bead. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Valox® V2105U PBT (Europe-Africa-Middle East) Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | ISO75-1/-2 |
| Suzhou Hipro Polymers Hiprolon® 11ESNNHL P20 Nylon, dry Hiprolon® 11ESNNHL P20 long chain polyamide compound contains a bio-renewable resource. It features low density, low water absorbing, high dimension stability and heat stability, high cold impact.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | ISO 75-2 |
| Borealis Daplen™ EH104AE Polypropylene TPO Compound Daplen™ EH104AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness, high.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 °C | 117 °F | ISO 75-2/Af |
| ExxonMobil Exxtral™ H1025 Performance Polyolefin Product Description: A specialty thermoplastic olefin resin with good flow, cold temperature impact resistance, low CLTE, and excellent paintability for automotive exterior applications.Availability.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® R 47 HW 10 PA6 Grilon R 47 HW 10 is a flexible, cold impact resistant and heat stabilized polyamide 6 for applications in the extrusion. The material can be processed on all for polyamides suitable tube-extrusion .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 °C | 117 °F | ISO 75-2/A |
| ExxonMobil PP7033L1 Polypropylene Impact Copolymer Product Description: An impact copolymer resin characterized with low flow. It is suitable for extrusion applications like sheet and thermoforming. It is also suitable for molding applications like.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® RS LC1201 BK040A Nylon 1010
(Unverified Data**) Toughened Renewably Sourced Medium Viscosity Polyamide 1010 Developed for Extrusion Zytel RS LC1201 BK040A is a renewably sourced polyamide 1010 resin containing a minimum of 85% renewably sourced i.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® ST811HS NC010 Nylon 6
(Unverified Data**) Zytel® ST811HS is a flexible, heat stabilized Super Tough polyamide 6 resin developed for extrusion and injection molding applications such as cable and rope jacketing, hose inner cores and fastene.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.2 °C | 117 °F | |
| Aclo Accutech Polypropylene Copolymer CP0437C20L1 Calcium Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | |
| Arkema Group Rilsan® BESN P20 TL Nylon 11, Flexible Tubing Grade (Conditioned) Designation ISO 1874-PA11-P,EHL,22-004Flexible grade for tubes extrusion. Available color: black and natural. Light and heat stabilized.Flexibility. High impact strength. Very good chemical resistan.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | |
| Arkema Group Rilsan® BMN P20 D Nylon 11 (Conditioned) Designation ISO 1874-PA11-P,MR,12-004Flexible grade for injection molding. Available colors: black and natural. Mold release agent.Outstanding working properties. Easy filling of the mold due to its.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® LC6210 BK010 Nylon 612
(Unverified Data**) Zytel® LC6210 BK010 is a highly toughened, heat stabilized polyamide 612 for extrusion, blow molding or processing by other techniques requiring high melt viscosity. It was previously coded Zytel®.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | CP-TM-12 |
| PolyOne Elastamax HTE 2101-1002 Polyurethane Alloy
(discontinued **) This is an extrusion grade polyurethane alloy. Physical Form: Pellet. Standard Color: Off white, opaque.Information provided by M. A. Hanna. M. A. Hanna and Geon merged to form PolyOne in 2000. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C @Thickness 3.20 mm |
117 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® X6800BM PBT (Europe-Africa-Middle East) Blow moldable, impact modifed XENOY |
|||