- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 278 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 278 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | ASTM D648 |
| Quadrant EPP Duratron® PAI T4203 Extruded Polyamide-imide (ASTM Product Data Sheet) |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C @Thickness 3.20 mm |
532 °F @Thickness 0.126 in |
Annealed; 2 hours at 200°C; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-755 SL45 Polyaryletherketone (PAEK)
(Unverified Data**) AV-755 SL45 is a wear resistant grade of AvaSpire polyaryletherketone (PAEK) designed to provide low wear rates and high pressure-velocity (PV) tolerance in lubricated wear environments. Like the ot.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | ASTM D648 |
| Quadrant EPP Duratron® PAI T4503 Compression Molded, Polyamide-imide, Eelectrical Grade (ASTM Product Data Sheet) |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | ASTM D648 |
| Quadrant EPP Semitron® CMP XL20 (ASTM Product Data Sheet) |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Torlon® 4200 Polyamide-imide (PAI)
(Unverified Data**) Torlon 4200 is an unreinforced, unpigmented grade of polyamide-imide (PAI) resin for extrusion. This grade is designed for applications in the semiconductor industry which cannot tolerate particulat.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Torlon® 4203L Polyamide-imide (PAI)
(Unverified Data**) Torlon 4203L is an unreinforced, lubricated, pigmented grade of polyamide-imide (PAI) resin. It has the best impact resistance and greatest elongation of all the Torlon grades. Torlon PAI has the hi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI)
(Unverified Data**) Torlon 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not only.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear (Europe-Africa-Middle East) LNP* Lubricomp* OCL4036L is a compound based on PPS - Linear resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP OCL36XXP PPS - Linear (Europe-Africa-Middle East) LNP* LUBRICOMP* OCL36XXP is a compound based on PPS- Linear resin containing PTFE, Carbon Fiber. Added features include : Internally Lubricated, Electrically Conductive . |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA), 65% GlassMineral (Dry) Amodel® AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifica.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; Flatwise; ISO 75-2/A |
| Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA), 33% Glass Fiber Amodel® AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C @Thickness 3.20 mm |
532 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-755 SL45 Polyaryletherketone (PAEK) AV-755 SL45 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates and high pressure-velocity (PV) tolerance in lubricated wear environments. Like th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers KetaSpire® KT-880 GF15 Polyetheretherketone (PEEK), 15% Glass Fiber KetaSpire® KT-880 GF15 is a high flow, 15% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Torlon® 4200 Polyamide-imide (PAI) Torlon® 4200 is an unreinforced, unpigmented grade of polyamide-imide (PAI) resin for extrusion. This grade is designed for applications in the semiconductor industry which cannot tolerate partic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Torlon® 4203L Polyamide-imide (PAI) Torlon® 4203L is an unreinforced, lubricated, pigmented grade of polyamide-imide (PAI) resin. It has the best impact resistance and greatest elongation of all the Torlon® grades. Torlon® PA.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Torlon® 4435 Polyamide-imide (PAI) Torlon® 4435 is a polyamide-imide resin specifically designed to provide exceptionally low wear performance in non-lubricated applications even at high pressure and velocity (PV) conditions. Not .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C @Thickness 3.20 mm |
532 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp LF004 PEEK LNP THERMOCOMP* LF004 is a compound based on Polyetheretherketone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | ASTM D648 |
| Plenco 6990 Phenolic, Briquette, Transfer Molded PLENCO 06990 is a glass and mineral filled novolac phenolic molding compound. UL recognized under component file E40654.Information supplied by Plenco. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | ASTM D648 |
| Ensinger TECATOR™ TI 5013 Polyamide-imide (PAI) TECATOR™ is a high performance melt processable polyamideimide that maintains its excellent mechanical and wear properties in temperature environments exceeding 500°F. Stock shapes from Ensinger .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers Torlon® 4203 Polyamide-imide (PAI)
(discontinued **) Torlon 4203 is an unreinforced, lubricated, pigmented grade of polyamide-imide (PAI) resin for extrusion. It has the best impact resistance and greatest elongation of all the Torlon grades. Torlon P.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Unannealed; ISO 75-2/Af |
| Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material excee.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | ASTM D648 |
| Plenco 1581 Polyester, Briquette, Transfer Molded PLENCO 01581 is a glass and mineral reinforced pelletized polyester molding compound, exhibiting excellent dimensional stability, mechanical strength and also arc resistance, track resistance, and f.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | |
| Isoflon PAI Polyamideimide Materials with strong mechanical and electrical performances under high temperatures.Information provided by Isoflon. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | ASTM D648 |
| Solvay Specialty Polymers Xydar® MG-350 Liquid Crystal Polymer, Mineral and Glass Filled
(discontinued **)< XYDAR MG-350 Liquid Crystal Polymer (LCP) is a mineral and glass-filled injection molding grade developed specifically for cost-effective performance in applications where a balance of flatness and .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 278 °C | 532 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AS-1566 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1566 HS resin is a 65% glass and mineral reinforced polyphthalamide (PPA) resin that exhibits a high deflection temperature and high flexural modulus. This grade was designed specifically .. |
|||