- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 545 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 545 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® HTN 52G35HSL BK083 Polyphthalamide (PPA)
(Unverified Data**) Zytel® HTN52G35HSL BK083 is a 35% glass reinforced, heat stabilized, lubricated high performance polyamide resin that can be molded in water heated molds. It is also a PPA resin.Information provid.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.18 mm |
545 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-750 GF40 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire AV-750 GF40 is a 40% glass reinforced polyaryletherketone (PAEK) designed to fill the marketplace need for a lower-priced PEEK (polyetheretherketone). This resin provides the typical chemic.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | |
| Lehmann & Voss LUVOCOM® 1105-8278/GY PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Ch.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | |
| Lehmann & Voss LUVOCOM® 19-7660 Polyamide 46, with glass fiber, PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Highly dimensionally stable at elevated temperatures.Gear parts for automot.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | |
| Lehmann & Voss LUVOCOM® 19-7669 Polyamide 46, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Highly dimensionally stable at elevated temperatures.Gear parts for automot.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ASTM D648 |
| Kuraray Genestarâ„¢ GW2458HF Nylon, 45% Glass Filled Low Warpage, High Flow V-0 Grade. It is suited for low warpage and high flow applications, making it well suited for card connectors. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | |
| Lehmann & Voss LUVOCOM® 1105-0948/YL2 PEEK, with glass fiber Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; impact resistance.Dynamic stressed parts at high movement velocity.Ch.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ISO 75-2/A |
| Solvay Specialty Polymers Amodel® A-1130 FW Polyphthalamide (PPA), 30% Glass Fiber Amodel® A-1130 FW is a 30% glass-fiber reinforced polyphthalamide (PPA) grade containing a solid lubricant. This resin was designed for moderate-pressure, low-velocity friction and wear applicati.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber Amodel® AE-1133 is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) designed to work in the modern automotive electrical environment. It has a high heat deflection temperature, high .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® AS-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA4/6 CF30 30% Carbon Filled (Dry) Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 30% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedInformation provided by TP Composites.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA4/6 M/GF 20 HS 20% Glass/Mineral Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Mineral, 50% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA4/6 CF30 TL15 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance and Low FrictionInformation p.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP UF00ASW PPA LNP* Thermocomp* UF00ASW is a compound based on Polyphthalamide (PPA) containing glass fiber. Characteristics of this grade of Heat Stabilized and Hot Water Moldable. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C @Thickness 3.20 mm |
545 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | dry; ISO 75-1/-2 |
| DSM Stanyl® TW242FM10 PA46-(GF+MF)50 50% Glass/Mineral Reinforced, Heat Stabilized |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | dry; ISO 75-1/-2 |
| DSM Stanyl® TW278F10 (PA46+PTFE)-GF50 50% Glass Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HTV-45H1 black 9205 PA6T/6I-GF45 Product description: Grivory HTV-45H1 black 9205 is a 45% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Polymer designation a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT1V-5 FWA nat PA6T/6I-GF50 Product description: Grivory HT1V-5 FWA natural is a 50 wt.-% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® HT1V-5 HY black 9205 PA6T/6I-GF50 Product description: Grivory HT1V-5 HY black 9205 is a 50% glass-fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT1V-5 HY bl.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | HDT/A; ISO 75-1/2 |
| Akro-Plastic Akromid® T1 GF 30 (3466) PPA Dry, 30% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | HDT/A; ISO 75-1/2 |
| Akro-Plastic Akromid® T1 GF 50 (3101) PPA Dry, 50% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | HDT/A; ISO 75-1/2 |
| Akro-Plastic Akromid® T1 GF 40 (3464) PPA Dry, 40% Glass Filled The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ASTM D648 |
| Kuraray Genestar™ GR2300 Nylon, 30% Glass Filled Standard V-0 Grade. Delivers increased fluidity and weld strength. Well suited for a wide range of electrical and electronic components. |
|||