DuPont Performance Polymers Zytel® HTN 52G35HSL BK083 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 52G35HSL BK083 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zytel® HTN52G35HSL BK083 is a 35% glass reinforced, heat stabilized, lubricated high performance polyamide resin that can be molded in water heated molds. It is also a PPA resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
DAM; ISO 1183
Filler Content 35 %
35 %
DAM
Water Absorption 0.50 %

@Temperature 23.0 °C
0.50 %

@Temperature 73.4 °F
Immersion 24h; DAM; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Thickness 2.00 mm
0.0030 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm

@Thickness 2.00 mm
0.0090 in/in

@Thickness 0.0787 in
DAM; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 187 MPa

@Temperature 23.0 °C
27100 psi

@Temperature 73.4 °F
DAM; ISO 527
Elongation at Break 2.1 %

@Temperature 23.0 °C
2.1 %

@Temperature 73.4 °F
DAM; ISO 527
Tensile Modulus 11.6 GPa

@Temperature 23.0 °C
1680 ksi

@Temperature 73.4 °F
DAM; ISO 527
Flexural Modulus 10.3 GPa

@Temperature 23.0 °C
1490 ksi

@Temperature 73.4 °F
DAM; ISO 178
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
50%RH; ISO 179/1eU
4.00 J/cm²

@Temperature -30.0 °C
19.0 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 179/1eU
4.50 J/cm²

@Temperature 23.0 °C
21.4 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
50%RH; ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 179/1eA
0.800 J/cm²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
278 µin/in-°F

@Temperature -40.0 - 73.4 °F
DAM; ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
278 µin/in-°F

@Temperature 73.4 - 131 °F
DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow 61.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
33.9 µin/in-°F

@Temperature -40.0 - 73.4 °F
DAM; ISO 11359-1/-2
67.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
37.2 µin/in-°F

@Temperature 73.4 - 131 °F
DAM; ISO 11359-1/-2
80.0 µm/m-°C

@Temperature 55.0 - 160 °C
44.4 µin/in-°F

@Temperature 131 - 320 °F
DAM; ISO 11359-1/-2
Melting Point 310 °C
590 °F
10°C/min, First Heat; DAM; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 285 °C
545 °F
DAM; ISO 75-1/-2
UL RTI, Electrical 150 °C

@Thickness 0.750 mm
302 °F

@Thickness 0.0295 in
DAM; UL 746B
150 °C

@Thickness 1.50 mm
302 °F

@Thickness 0.0591 in
DAM; UL 746B
150 °C

@Thickness 3.00 mm
302 °F

@Thickness 0.118 in
DAM; UL 746B
UL RTI, Mechanical with Impact 125 °C

@Thickness 0.750 mm
257 °F

@Thickness 0.0295 in
DAM; UL 746B
125 °C

@Thickness 3.00 mm
257 °F

@Thickness 0.118 in
DAM; UL 746B
UL RTI, Mechanical without Impact 130 °C

@Thickness 0.750 mm
266 °F

@Thickness 0.0295 in
DAM; UL 746B
150 °C

@Thickness 3.00 mm
302 °F

@Thickness 0.118 in
DAM; UL 746B
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
DAM; IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
DAM; IEC 60695-11-10
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; IEC 60695-11-10
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
DAM; UL94
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
DAM; UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
DAM; UL94
Glow Wire Test 700 °C

@Thickness 1.50 mm
1290 °F

@Thickness 0.0591 in
DAM; IEC 60695-2-12
725 °C

@Thickness 1.50 mm
1340 °F

@Thickness 0.0591 in
DAM; Ignition; IEC 60695-2-13
750 °C

@Thickness 0.750 mm
1380 °F

@Thickness 0.0295 in
DAM; IEC 60695-2-12
775 °C

@Thickness 0.750 mm
1430 °F

@Thickness 0.0295 in
DAM; Ignition; IEC 60695-2-13
775 °C

@Thickness 3.00 mm
1430 °F

@Thickness 0.118 in
DAM; Ignition; IEC 60695-2-13
850 °C

@Thickness 3.00 mm
1560 °F

@Thickness 0.118 in
DAM; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm

@Temperature 23.0 °C
1.00e+15 ohm-cm

@Temperature 73.4 °F
DAM; IEC 60093
Surface Resistance >= 1.00e+15 ohm

@Temperature 23.0 °C
>= 1.00e+15 ohm

@Temperature 73.4 °F
DAM; IEC 60093
Processing Properties Metric English Comments
Melt Temperature 325 °C
617 °F
DAM; Optimum
320 - 330 °C
608 - 626 °F
DAM
Mold Temperature 85.0 - 105 °C
185 - 221 °F
DAM
Drying Temperature 100 °C
212 °F
DAM
Dry Time 6.00 - 8.00 hour
6.00 - 8.00 hour
DAM
Moisture Content <= 0.10 %
<= 0.10 %
DAM
Descriptive Properties Value Comments
Additive Heat Stabilizer
DAM
Lubricant
DAM
Appearance Black Color
DAM
Filler Glass Reinforced
DAM
Forms Pellets
DAM
Generic Polyphthalamide (PPA)
DAM
Material Status Current
DAM
Part Marking Code >PA6T/66-GF35<
ISO 11469; DAM
>PPA-GF35<
SAE J1344; DAM
Polymer Family High performance polyamide
DAM
Polymer Type Partially Aromatic PA, PPA
DAM
Processing Method Injection Molding
DAM
Product Category Glass Reinforced Resins
DAM
Region Available - Global Yes
DAM
Resin Identification PA6T/66-GF35
ISO 1043; DAM
RoHS Compliance Contact Manufacturer
DAM