Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 11.0 - 500 µm/m-°C @Temperature 55.0 - 250 °C |
6.11 - 278 µin/in-°F @Temperature 131 - 482 °F |
Average value: 122 µm/m-°C Grade Count:8 |
Overview of materials for Polyphthalamide (PPA), 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 438E0V16304 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 4%. Weight loss on heating = 0.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 465E2R30012 Natural, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 12%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 100 °C |
6.11 µin/in-°F @Temperature 68.0 - 212 °F |
|
Special Metals NIMONIC® Alloy 75 A nickel-chromium alloy with good mechanical properties and oxidation resistance at high temperatures. Used for sheet-metal fabrications in gas-turbine engines, for components of industrial furnace.. |
|||
CTE, linear | 11.0 µm/m-°C @Temperature 20.0 °C |
6.11 µin/in-°F @Temperature 68.0 °F |
ASTM D 696 |
Lubrizol Isoplast® 101LGF60BLK Engineering Thermoplastic Polyurethane Resin Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
CTE, linear | 11.0 µm/m-°C @Temperature 20.0 °C |
6.11 µin/in-°F @Temperature 68.0 °F |
|
Goodfellow E-glass/Epoxy Composite Boro-silicate glass/EpoxyInformation provided by Goodfellow. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 264E0096908 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 22%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 264E4861310 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 10%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE Butyrate 264E0096908 Natural, Trsp TENITE cellulosic plastic.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 285A2R30016 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 8%. Weight loss on heating = 0.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 285A2R30023 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 485E2R30010 Natural, Trsp Cellulose Acetate Butyrate Plasticizer 10%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 565A3720023 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 23%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 575E3720010 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Propionate 307A2R30013 Natural, Trsp Cellulose Acetate Propionate Plasticizer 16%. Weight loss on heating = 0.8% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Propionate 350E0096912 Natural, Trsp Cellulose Acetate Propionate Plasticizer 13%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Propionate 376E4000012 Clear, Trsp Cellulose Acetate Propionate Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Propionate 377E4861312 Clear, Trsp Cellulose Acetate Propionate Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Propionate 380A4000010 Clear, Trsp Cellulose Acetate Propionate Plasticizer 10%. Weight loss on heating = 0.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Propionate 383A2R30009 Natural, Trsp Cellulose Acetate Propionate Plasticizer 9%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of pr.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Propionate 383A2R30012 Natural, Trsp Cellulose Acetate Propionate Plasticizer 12%. Weight loss on heating = 0.4% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
CTE, linear | 11.0 - 12.0 µm/m-°C @Temperature 1000 °C |
6.11 - 6.67 µin/in-°F @Temperature 1830 °F |
|
Chosun Refractories CUN-198 Nozzle Brick Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET). |
|||
CTE, linear | 11.0 - 13.0 µm/m-°C @Temperature 1000 °C |
6.11 - 7.22 µin/in-°F @Temperature 1830 °F |
|
Chosun Refractories HRD-SNE Plate Brick Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET). |
|||
CTE, linear | 11.0 - 13.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 7.22 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance A-2 Alnico Magnetic Material |
|||
CTE, linear | 11.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C |
6.11 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F |
ISO 11359 |
Ascend Performance Materials Vydyne® 50BW Nylon 66, Dry as Molded Vydyne® 50BW is a general purpose Nylon 66 resin. Available in natural. Designed for extrusion applications that do not require use of a high-viscosity resin. This resin offers a well-balanced comb.. |
|||
CTE, linear | 11.0 - 13.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 7.22 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance A-5-7 Alnico Magnetic Material |
|||
CTE, linear | 11.0 - 13.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 7.22 µin/in-°F @Temperature 68.0 °F |
Parallel DOM |
Alliance A-5DG Alnico Magnetic Material |
|||
CTE, linear | 11.0 - 170 µm/m-°C | 6.11 - 94.4 µin/in-°F | Average value: 76.9 µm/m-°C Grade Count:12 |
Overview of materials for Cellulose Acetate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate, Molded". Each property range of values reported is minimum and maximum values of appr.. |
|||
CTE, linear | 11.0 - 170 µm/m-°C | 6.11 - 94.4 µin/in-°F | Average value: 44.8 µm/m-°C Grade Count:36 |
Overview of materials for Cellulose Acetate Butyrate, Molded This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Butyrate, Molded". Each property range of values reported is minimum and maximum value.. |
|||
CTE, linear | 11.0 - 17.0 µm/m-°C @Temperature 20.0 °C |
6.11 - 9.44 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Eastman Tenite Butyrate 465A3720010 Clear, Trsp Cellulose Acetate Butyrate
(discontinued **) Plasticizer 10%. Weight loss on heating = 0.9% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |