- Polymer Property : Maximum Service Temperature, Air = 293 °F
Polymer Property : Maximum Service Temperature, Air = 293 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 145 °C | 293 °F | short period, no load |
| Omnia Plastica Akulon® POM h Acetal Homopolymer The general features of homopolymer acetalic resin are similar to those of copolymer POM c, except that service temperature (under load) is slightly higher but resistance to hydrolysis and strong al.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | Continuous; FRISETTA Test Method |
| Nilit FRIANYL B63 TF-GV 1520 Nylon 6 for injection molding, 15% PTFE lubricated, 20% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | <20000 hours; IEC 60216-P1 |
| Hexion Bakelite™ PF 2137 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof
(discontinued ** Phenolic molding compound, inorganically/organically filled, glass fiber reinforced, increased heat resistance, minimal distortion, dish washer proof.Application areas: Iron heat shields, fittings f.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | <20000 hours; IEC 60216-P1 |
| Hexion Bakelite™ PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof, UL Listed
(disc Phenolic molding compound, inorganically/organically filled, average heat resistance, increased dimensional stability, dish washer proof, UL listed molding compound 1.5 mm/V-0 (ALL).Application area.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Industrial Laminates/Norplex NP313 Cotton Fabric Description: Canvas phenolic laminate with molybdenum disulfide lubricant. Mechanical properties slightly lower than NP310.Thickness Tested: 0.062", 0.125" & 0.500" |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| LATI Laramid G/35 PPA, 35% Glass Fiber Reinforced Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; .. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | Short peaks operation |
| Polyram PlusTek PD305G6 Nylon 12 for Injection Molding, 30% Glass-fiber Reinforced 30% Glass-fiber reinforced Nylon 12 for injection molding applications.Information provided by Polyram. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA16 Food and Drug Application Epoxy Adhesive TRA-BOND FDA-16 EPOXY ADHESIVE is a medium viscosity epoxy resin system specifically developed for medical device applications. It has been tested in accordance with USP biological reactivity tests,.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA2 Food and Drug Application Epoxy Adhesive TRA-BOND FDA-2 is a medium viscosity epoxy resin system specifically developed for medical device applications. It has been tested in accordance with USP biological reactivity tests, in vivo and rec.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA22 Food and Drug Application Epoxy Adhesive TRA-BOND FDA-22 is a high viscosity epoxy resin system specifically developed for bonding and coating applications in accordance with Title 21, U.S. Code of Federal Regulations, Food and Drug Admini.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA23 Food and Drug Application Epoxy Adhesive TRA-BOND FDA-23 is a high viscosity epoxy resin system specifically developed for bonding and coating applications in accordance with Title 21, U.S. Code of Federal Regulations, Food and Drug Admini.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond FDA8 Food and Drug Application Epoxy Adhesive TRA-BOND FDA-8 EPOXY ADHESIVE is a low viscosity epoxy resin system specifically developed for bonding and coating applications in accordance with Title 21, U.S. Code of Federal Regulations, Food an.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Cast 3103 General Purpose Epoxy Casting Compound TRA-CAST 3103 is a low viscosity two-part formulation recommended for general purpose electrical potting and encapsulating application where the combination of good mechanical thermal and electrical.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Cast 3108 General Purpose Epoxy Casting Compound TRA-CAST 3108 is a low viscosity two-part formulation recommended for underfill and encapsulating applications where the combination of good mechanical thermal and electrical properties are required.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Cast 3113 General Purpose Epoxy Casting Compound TRA-CAST 3113 is a low viscosity two-part formulation recommended for general purpose electrical potting and encapsulating applications where the combination of good mechanical thermal and electrica.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Tra-Con Tra-Bond RO7 Radio Opaque Epoxy Adhesive TRA-BOND RO-7 is a high viscosity epoxy resin system specifically developed for adhesive and coating applications where radio opacity is required. It can be used as an X-ray marker on in-vitro medic.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | few hours; VDE 0304/P2-1, IEC 216 |
| EPICHEM Epilon G2-PC 10% GF Polycarbonate, 10% Glass Fiber Characteristics: 10% glass fibre filled, good mechanical properties |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | few hours; VDE 0304/P2-1, IEC 216 |
| EPICHEM Epilon G4-PC 20% GF Polycarbonate, 20% Glass Fiber Characteristics: 20% glass fibre filled, excellent mechanical properties |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | 5000 h; VDE 0304/P2-1, IEC 216 |
| EPICHEM Epilon PC GF 10 V0 Polycarbonate, 10% Glass Fiber Characteristics: self-extinguishing V0 at 1,6 mm, 10% glass fibre filled |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG7 BK 00564 35% Glass Filled PA6 (Conditioned) Description: 35% glass-fiber reinforced and heat aging resistant injection-molding grade, e.g. for automotive manifolds and pedals.Information provided by BASF |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Atom Adhesives AA-BOND FDA2 Epoxy Adhesive AA-BOND FDA2 is a medium viscosity epoxy resin system specifically developed for medical device applications. It has been tested in accordance with USP biological reactivity tests, in vivo and recei.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Atom Adhesives AA-BOND FDA22 Epoxy Adhesive AA-BOND FDA22 is a high viscosity epoxy resin system specifically developed for bonding and coating applications in accordance with Title 21, U.S. Code of Federal Regulations, Food and Drug Administ.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | |
| Atom Adhesives AA-BOND FDA2T Epoxy Adhesive AA-BOND FDA2T is a thixotropic epoxy resin system specifically developed for medical device applications. It has been tested in accordance with USP biological reactivity tests, in vivo and received .. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20,000 hr |
| BASF Ultramid® A3WG5 25% Glass Filled PA66 (Conditioned) Ultramid A3WG5 is a 25% glass fiber reinforced and heat resistance injection molding PA66 grade. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20,000 hr |
| BASF Ultramid® B3WG6 BK00564 30% Glass Filled PA6 (Conditioned) Ultramid B3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG10 BK 00564 50% Glass Filled PA6 (Conditioned) Description: 50% glass-fiber reinforced and heat aging resistant injection-molding grade for technical parts with very high stiffness.Information provided by BASF |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG10 BK 00564 50% Glass Filled PA6 (Dry) Description: 50% glass-fiber reinforced and heat aging resistant injection-molding grade for technical parts with very high stiffness.Information provided by BASF |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG5 25% Glass Filled PA6 (Conditioned) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |
|||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr |
| BASF Ultramid® B3WG5 BK 00654 PA6 25% Glass Filled BK (Dry) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |
|||