BASF Ultramid® B3WG5 25% Glass Filled PA6 (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3WG5 25% Glass Filled PA6 (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and electrical insulating parts.Information provided by BASF
Physical Properties Metric English Comments
Bulk Density 0.500 - 0.800 g/cc
0.0181 - 0.0289 lb/in³
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Water Absorption 6.8 - 7.4 %
6.8 - 7.4 %
Saturation; ISO 62
Moisture Absorption at Equilibrium 2.1 - 2.5 %
2.1 - 2.5 %
23°C; 50% RH; ISO 62
2.3 %
2.3 %
50% RH
7.1 %
7.1 %
Saturation
Viscosity Measurement 140
140
ISO 307
Linear Mold Shrinkage 0.0035 cm/cm
0.0035 in/in
restricted
Melt Flow 72.6 g/10 min

@Load 5.00 kg,
Temperature 275 °C
72.6 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 105 MPa
15200 psi
50 mm/min; ISO 527-1/-2
Elongation at Yield 8.5 %
8.5 %
50 mm/min; ISO 527-1/-2
Modulus of Elasticity 5.00 GPa
725 ksi
ISO 527-1/-2
Flexural Strength 150 MPa
21800 psi
at max force; ISO 178
Flexural Modulus 4.20 GPa
609 ksi
ISO 178
Izod Impact, Notched (ISO) 17.0 kJ/m²

@Temperature 23.0 °C
8.09 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 10.5 J/cm²

@Temperature 23.0 °C
50.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 2.50 J/cm²

@Temperature 23.0 °C
11.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 3000 MPa

@Strain <=0.500 %
435000 psi

@Strain <=0.500 %
ISO 899-1
Thermal Properties Metric English Comments
Specific Heat Capacity 1.50 J/g-°C
0.359 BTU/lb-°F
Thermal Conductivity 0.350 W/m-K
2.43 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53765
Maximum Service Temperature, Air 145 °C
293 °F
for 50% loss of tensile strength after 20000hr
175 °C
347 °F
for 50% loss of tensile strength after 5000hr
200 °C
392 °F
Decomposition Temperature >= 300 °C
>= 572 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093
Dielectric Constant 7.0

@Frequency 1.00 Hz
7.0

@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.24

@Frequency 1.00e+6 Hz
0.24

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 450 V
450 V
Test solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 80.0 °C
176 °F
Hopper Throat
Zone 1 260 °C
500 °F
Feed Zone
Zone 2 270 °C
518 °F
Compression
Zone 3 280 °C
536 °F
Metering-zone
Zone 4 280 °C
536 °F
Nozzle
Melt Temperature 270 - 290 °C
518 - 554 °F
Injection-molding/Extrusion
280 °C
536 °F
Optimal
Mold Temperature 80.0 °C
176 °F
Optimal
80.0 - 90.0 °C
176 - 194 °F
Injection-molding
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Optimal
<= 0.15 %
<= 0.15 %
Descriptive Properties Value Comments
Commercial Status Europe
Ignition Temperature >400°C
ASTM D129
Peripheral screw speed < 0.3 m/s