Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 2400 min @Temperature 16.0 °C |
40.0 hour @Temperature 60.8 °F |
Full Load |
Chesterton ARC CS4 low-viscosity, 100% solids, barrier coating Description: An advanced composite formulated to protect concrete surfaces from harsh chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat in a 2 coat syst.. |
|||
Cure Time | 2400 min @Temperature 32.0 °C |
40.0 hour @Temperature 89.6 °F |
Overcoat End |
Chesterton ARC HT-T Spark Testable High Temperature Trowelable Abrasion Control Compound An advanced ceramic composite formulated to protect equipment from corrosion and erosion in elevated temperature water solution immersion. This system is a high viscosity composite that is applied b.. |
|||
Cure Time | 2400 min @Temperature 25.0 °C |
40.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton ARC MX1 Vertical Build Extreme Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It is applied at a thickness of 6 mm (1/4”).. |
|||
Cure Time | 2400 min @Temperature 10.0 °C |
40.0 hour @Temperature 50.0 °F |
Overcoat End |
Chesterton ARC S2 Ceramic reinforced erosion resistant coating Description: An advanced ceramic composite for the resurfacing and protection of all metal surfaces. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrinking, 100% soli.. |
|||
Cure Time | 2400 min @Temperature 10.0 °C |
40.0 hour @Temperature 50.0 °F |
Overcoat End |
Chesterton ARC SD4i High temperature ceramic reinforced erosion resistant coating Description: An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10-15 mils) per coat.. |
|||
Cure Time | 2400 min @Temperature 10.0 °C |
40.0 hour @Temperature 50.0 °F |
Overcoat End |
Chesterton MRS S2 Metal Rebuilding System An advanced ceramic composite for the resurfacing and protection of all metal surfaces. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrinking, 100% solids. MRS S2 is.. |
|||
Cure Time | 2400 min @Temperature 10.0 °C |
40.0 hour @Temperature 50.0 °F |
Overcoat End |
Chesterton MRS SD4i Metal Rebuilding System An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10 – 15 mils) per coat. Non-shri.. |
|||
Cure Time | 2400 min @Temperature 25.0 °C |
40.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton ARC MXC Castable Extreme Wear Compound Description: An advanced ceramic composite, with flowable viscosity, for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It can be hand tro.. |
|||
Cure Time | 2400 min @Temperature 16.0 °C |
40.0 hour @Temperature 60.8 °F |
Full Load |
Chesterton ARC CS2 Low-viscosity, Composite concrete primer sealer Description: An advanced composite formulated to protect concrete surfaces from mild chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat. Non-shrinking. 1.. |
|||
Cure Time | 2400 min @Temperature 10.0 °C |
40.0 hour @Temperature 50.0 °F |
Light Load |
Chesterton ARC S1HB Sprayable high-viscosity, 100% solids, advanced coating An advanced composite formulated to protect concrete and metal surfaces from corrosion and chemical attack. It is normally applied at a thickness of 1-2 mm (40-80 mils) per coat. However, greater si.. |