Chesterton ARC MX1 Vertical Build Extreme Wear Compound

Category Ceramic , Polymer , Thermoset , Epoxy
Manufacturer Chesterton
Trade Name ARC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chesterton ARC MX1 Vertical Build Extreme Wear Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It is applied at a thickness of 6 mm (1/4”) or more. Non-Shrinking, 100% solids. ARC MX1 is formulated with a high concentration of ceramic beads and fine ceramic particles for extremely abrasive environments where superior protection is desirable. ARC MX1 is applied to a primed surface by trowel or it may be molded where close tolerances and a smooth finish are necessary. It is chosen over ARC 890 and 897 when increased abrasion protection is required. Benefits: Outlasts other wear resistant materials and coatings by 5-7 times.Excellent wear characteristics extend equipments’ operating cyclesOutwears weld overlay or ceramic tilesTough resin structure resists thermal-mechanical shockMay be molded to precise dimensions for critical tolerancesPerforms well under fluctuating chemical environments. Suggested Uses:PulverizersDredge PumpsHoppers and SilosTile Lined Conveyor ScrewsCD4/Ni-Hard/Hordox Slurry pumps and pipe ElbowsFans/Blowers/CyclonesTransport Pipelines for AbrasivesMetal Clad Exhaust Fan HousingCeramic Tile Lined ChutesCeramic Tile or Rubber Lined Deflector Hoods Information provided by Chesterton
Physical Properties Metric English Comments
Density 2.70 g/cc
0.0975 lb/in³
Cured
Mechanical Properties Metric English Comments
Hardness, Shore D 89
89
ASTM D2240
Tensile Strength at Break 20.7 MPa
3000 psi
ASTM D638
Flexural Strength 47.6 MPa
6900 psi
ASTM D790
Compressive Strength 110 MPa
16000 psi
ASTM D695
Impact Test 9.04 J
6.67 ft-lb
Reverse; ASTM D2794
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 95.0 °C
203 °F
Wet Service
205 °C
401 °F
Dry Service
Processing Properties Metric English Comments
Cure Time 60.0 min

@Temperature 32.0 °C
1.00 hour

@Temperature 89.6 °F
Tack Free
120 min

@Temperature 25.0 °C
2.00 hour

@Temperature 77.0 °F
Tack Free
150 min

@Temperature 32.0 °C
2.50 hour

@Temperature 89.6 °F
Light Load
180 min

@Temperature 16.0 °C
3.00 hour

@Temperature 60.8 °F
Tack Free
210 min

@Temperature 25.0 °C
3.50 hour

@Temperature 77.0 °F
Light Load
300 min

@Temperature 10.0 °C
5.00 hour

@Temperature 50.0 °F
Tack Free
420 min

@Temperature 16.0 °C
7.00 hour

@Temperature 60.8 °F
Light Load
540 min

@Temperature 10.0 °C
9.00 hour

@Temperature 50.0 °F
Light Load
960 min

@Temperature 32.0 °C
16.0 hour

@Temperature 89.6 °F
Full Load
1200 min

@Temperature 25.0 °C
20.0 hour

@Temperature 77.0 °F
Full Load
1980 min

@Temperature 32.0 °C
33.0 hour

@Temperature 89.6 °F
Full Chemical
2160 min

@Temperature 16.0 °C
36.0 hour

@Temperature 60.8 °F
Full Load
2400 min

@Temperature 25.0 °C
40.0 hour

@Temperature 77.0 °F
Full Chemical
2880 min

@Temperature 10.0 °C
48.0 hour

@Temperature 50.0 °F
Full Load
4800 min

@Temperature 16.0 °C
80.0 hour

@Temperature 60.8 °F
Full Chemical
6480 min

@Temperature 10.0 °C
108 hour

@Temperature 50.0 °F
Full Chemical
Descriptive Properties Value Comments
Color Blue