3M Dyneon™ Aflas® FA-100H PTFE Fluoroelastomer  (discontinued **)

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ Aflas® FA-100H PTFE Fluoroelastomer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 57%F in polymer with 19% Medium Thermal Carbon Black (N990), 4% Triallyl Isocyanurate (TAIC), 1% Percadox™ 14, 1% Sodium Stearate. Compression molded goods in demanding environments (i.e. oilfield). Best resistance to gas blistering and extrusion under high differential pressures. Used in Aggressive Oil/Coolant/Base Resistant Applications.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
Oxygen Transmission 150 cc-mm/m²-24hr-atm
381 cc-mil/100 in²-24hr-atm
Mooney Viscosity 110

@Temperature 100 °C
110

@Temperature 212 °F
ML1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 71
71
Tensile Strength, Ultimate 19.0 MPa
2760 psi
Tensile Strength, Yield 2.80 MPa
406 psi
M100
Elongation at Break 375 %
375 %
Coefficient of Friction, Dynamic 0.70
0.70
Compression Set 50 %

@Temperature 200 °C
50 %

@Temperature 392 °F
70 hr; ASTM D395B
Thermal Properties Metric English Comments
CTE, linear 240 µm/m-°C

@Temperature 20.0 °C
133 µin/in-°F

@Temperature 68.0 °F
Specific Heat Capacity 1.67 J/g-°C
0.399 BTU/lb-°F
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
Glass Transition Temp, Tg 3.00 °C
37.4 °F
TR10
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 - 1.00e+16 ohm-cm
1.00e+15 - 1.00e+16 ohm-cm
Dielectric Constant 2.5

@Frequency 6.00e+7 Hz
2.5

@Frequency 6.00e+7 Hz
Dielectric Strength 23.0 kV/mm
584 kV/in