- Arkema Group Rilsan® AZM 23 G9 T6LD Nylon 12, 23% Glass Fiber Filled (Conditioned)
Arkema Group Rilsan® AZM 23 G9 T6LD Nylon 12, 23% Glass Fiber Filled (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 20% Glass Fiber Filled |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® AZM 23 G9 T6LD Nylon 12, 23% Glass Fiber Filled (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA12,MHLR,16-050,(G+C)(F+D)(23+05)Rigid grade with glass fiber (23%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stabilizing agent. Mold-release agent.Rigidity. Low friction coefficient. High compressive strength. Very low shrinkage: include 0,5% on average for the design of the mold. Low coefficient of linear expansion. High dimensional stability.Example applications: Mechanical parts with friction such as gear and bearing.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Melt Flow | 3.7 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.7 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 99.0 MPa | 14400 psi | 5 mm/min |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min |
| Tensile Modulus | 6.60 GPa | 957 ksi | 1 mm/min |
| Charpy Impact Unnotched | 7.03 J/cm² | 33.5 ft-lb/in² | |
| 7.28 J/cm² @Temperature -30.0 °C |
34.6 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.23 J/cm² | 5.85 ft-lb/in² | |
| 0.960 J/cm² @Temperature -30.0 °C |
4.57 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature 20.0 °C |
33.3 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 173 °C | 343 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| Vicat Softening Point | 165 °C | 329 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | |
| Comparative Tracking Index | 300 V | 300 V |