Arlon 55586XC028 0.0295" Cured/Uncured Silicone Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 55586XC028 0.0295" Cured/Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Cured Silicone RubberSubstrate: Style 162 FiberglassSide 2: Uncured Silicone RubberInterleave: 3 mil PEThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
Side 2 Silicone Property; Arlon SQA-TMS-024
1.56 g/cc
0.0564 lb/in³
Side 1 Silicone Property; Arlon SQA-TMS-024
Thickness 102 microns
4.00 mil
Side 1; Arlon SQA-TMS-003
165 microns
6.50 mil
Side 2; Arlon SQA-TMS-003
483 microns
19.0 mil
Substrate; Arlon SQA-TMS-003
749 microns
29.5 mil
Overall Thickness; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 37
37
Side 2 Silicone Property; ASTM D2240
55
55
Side 1 Silicone Property; ASTM D2240
Tensile Strength 3.65 MPa
530 psi
Side 1 Silicone Property; ASTM D412
6.55 MPa
950 psi
Side 2 Silicone Property; ASTM D412
Elongation at Break 300 %
300 %
Side 1 Silicone Property; ASTM D412
620 %
620 %
Side 2 Silicone Property; ASTM D412
Tear Strength 7.01 kN/m
40.0 pli
Side 1 Silicone Property; ASTM D624
26.3 kN/m
150 pli
Side 2 Silicone Property; ASTM D624
Peel Strength 2.49 kN/m
14.2 pli
Bond Strength; Arlon SQA-TMS-011
Thermal Properties Metric English Comments
Maximum Service Temperature, Inert 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
UL RTI, Electrical 200 °C
392 °F
E54153
UL RTI, Mechanical without Impact 200 °C
392 °F
E54153
Electrical Properties Metric English Comments
Dielectric Strength 21.3 kV/mm
540 kV/in
ASTM D149
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Post Cure Cycle
15.0 min

@Pressure 0.345 MPa,
Temperature 177 °C
0.250 hour

@Pressure 50.0 psi,
Temperature 350 °F
Recommended Cure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
Descriptive Properties Value Comments
Color Gray
Product
White
Substrate
Total Product Weight (oz/yd2) 38.5
Arlon SQA-TMS-025