BASF Petra® 130 30% Glass Filled PET

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer	BASF
Trade Name	Petra®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Petra® 130 30% Glass Filled PET.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Petra 130 is a 30% glass fiber reinforced polyethylene terephthalate (PET) for injection molding applications. It exhibits a good combination of performance properties including high strength and stiffness at elevated temperatures with good chemical resistance and dimensional stability.

Physical Properties	Metric	English	Comments
Density	1.32 g/cc	0.0477 lb/in³	Melt; ISO 1183
	1.55 g/cc	0.0560 lb/in³	ISO 1183
Viscosity Measurement	0.55	0.55	Inherent Viscosity
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM Test
Tensile Strength at Break	155 MPa	22500 psi	0.2 in/min; ASTM Test
	65.0 MPa @Temperature 120 °C	9430 psi @Temperature 248 °F	ISO Data
	65.0 MPa @Temperature 120 °C	9430 psi @Temperature 248 °F	ASTM Test
	80.0 MPa @Temperature 80.0 °C	11600 psi @Temperature 176 °F	ASTM Test
	80.0 MPa @Temperature 80.0 °C	11600 psi @Temperature 176 °F	ISO Data
	210 MPa @Temperature -40.0 °C	30500 psi @Temperature -40.0 °F	ISO Data
	210 MPa @Temperature -40.0 °C	30500 psi @Temperature -40.0 °F	ASTM Test
Tensile Strength, Ultimate	155 MPa	22500 psi	5mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	0.2 in/min; ASTM Test
	3.5 %	3.5 %	5mm/min; ISO 527
Tensile Modulus	10.2 GPa	1480 ksi	1mm/min; ISO 527
	2.94 GPa @Temperature 120 °C	426 ksi @Temperature 248 °F	ISO Data
	4.95 GPa @Temperature 80.0 °C	718 ksi @Temperature 176 °F	ISO Data
	10.4 GPa @Temperature -40.0 °C	1510 ksi @Temperature -40.0 °F	ISO Data
Flexural Strength	240 MPa	34800 psi	ASTM Test
	85.0 MPa @Temperature 120 °C	12300 psi @Temperature 248 °F	ASTM Test
	105 MPa @Temperature 93.0 °C	15200 psi @Temperature 199 °F	ASTM Test
	170 MPa @Temperature 65.0 °C	24700 psi @Temperature 149 °F	ASTM Test
	275 MPa @Temperature -40.0 °C	39900 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	8.97 GPa	1300 ksi	ASTM Test
	2.83 GPa @Temperature 120 °C	410 ksi @Temperature 248 °F	ASTM Test
	3.44 GPa @Temperature 93.0 °C	499 ksi @Temperature 199 °F	ASTM Test
	6.13 GPa @Temperature 65.0 °C	889 ksi @Temperature 149 °F	ASTM Test
Izod Impact, Notched	0.950 J/cm @Thickness 3.17 mm	1.78 ft-lb/in @Thickness 0.125 in	ASTM Test
Charpy Impact, Notched	0.900 J/cm²	4.28 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear	23.0 µm/m-°C @Temperature -30.0 - 30.0 °C	12.8 µin/in-°F @Temperature -22.0 - 86.0 °F	ASTM Test
CTE, linear, Parallel to Flow	23.0 µm/m-°C	12.8 µin/in-°F	ASTM Test
Specific Heat Capacity	2.287 J/g-°C	0.5466 BTU/lb-°F	Melt
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft²-°F	Melt
Melting Point	245 °C	473 °F	10 K/min
	245 °C	473 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	240 °C	464 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F	ISO 75
	220 °C	428 °F	ASTM Test
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Dielectric Constant	3.5 @Frequency 1.00e+6 Hz	3.5 @Frequency 1.00e+6 Hz	IEC 60250
	3.7 @Frequency 100 Hz	3.7 @Frequency 100 Hz	IEC 60250
Dielectric Strength	40.0 kV/mm	1020 kV/in	IEC 60243-1
Dissipation Factor	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	IEC 60250
	0.020 @Frequency 100 Hz	0.020 @Frequency 100 Hz	IEC 60250

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	115 °C	239 °F	Injection molding
Injection Velocity	115 mm/sec	4.53 in/sec	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes