- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 464 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 464 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 |
| Nilit FRIANYL B63 CV10 Nylon 6.6 for injection molding, 10% carbon fiber reinforced Nylon 6.6 for injection molding, good conductive and electrostatic properties.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | |
| Idemitsu Kosan Xarec® N WA 7020 SPS, 20% Glass Filled Crystalline Polymer Blend, Glass Filled, Impact Modified. Used in Automotive Electronics applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C @Thickness 6.40 mm |
464 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUMID GP3400B(W) PA66+MF40%, General Purpose Feature: Injection Molding, PA66+MF40%, General PurposeApplication: Automotive (Engine Cover)CAS No. 25038-54-4 and 14807-96-6Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Kolon KOPA® KN333MT30BL Mineral Reinforced Nylon 66 MF reinforcedApplications Cam shaftsInformation provided by API-Kolon. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | |
| LATI Latigray 66-01 CX/50 PA 66 Radiopaque compound based on Polyamide 66 (PA66). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | |
| LATI Latilub 57-10T Y/15 PPA, Aramid Reinforced Self-lubricating product based on Semi-aromatic polyamide (PPA). PTFE. Aramid fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by La.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | |
| LATI Latilub 66-10T Y/15 PA66, 15% Aramid Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyamide 66 (PA66). PTFE. Aramid fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP LC006 PEEK LNP THERMOCOMP* LC006 is a compound based on Polyetheretherketone resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK LNP THERMOCOMP* LF006 is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK LNP* THERMOCOMP* LF006E is a compound based on Polyetheretherketone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics NORYL GTX GTX8120P PPE+PA (Europe-Africa-Middle East) GTX8120P is a glass filled extrudable Noryl GTX with low thermal conductivity, suitable for thermal breaks |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C @Thickness 3.20 mm |
464 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP 2F004 FP-E (EFTE) LNP* FP-EF-1004 is a fluoropolymer compound based on ETFE resin containing 20% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics NORYL GTX GTX8408 PPE+PA Noryl GTX* GTX8408 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is glass filled and suitable for injection molding. The elongation of this material is higher than GTX8410W.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | DIN 53461 |
| Polyram PlusTek PA870G33 Nylon 6.6, 33% Glass Fiber 33% glass fiber reinforced, impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Toyobo VYLOPET® EMC310 Injection Molding Polyester Resin Applications: Coiled bobbinsMouthpiecesFeatures: High cyclesInformation provided by Toyobo. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Toyobo VYLOPET® EMC310TU Injection Molding Polyester Resin, Warpageless, High cycles Applications: Coiled bobbinsMouthpiecesFeatures: High cyclesWarpagelessInformation provided by Toyobo. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Toyobo Vylopet® EMC317R Glass Reinforced Polyester, Standard Grade Key Feature: UL-94 classApplications: Glossy surface componentsGeneral features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking resistance, ch.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM-D648 |
| Toyobo VYLOPET® EMC320R Polyester Resin VYLOPET® is a polyester resin developed specifically for injection molding. Polyester resins have excellent heat resistance, rigidity, chemical resistance, and electric properties. Grade EMC320R ha.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | DIN 53461 |
| Polyram PlusTek PA840G6 Nylon 6.6, 30% Glass Fiber 30% glass fiber reinforced, impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Cheng Yu Plastic N66C2 Nylon 66, 20% Mineral Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | dry; ISO 75-1/-2 |
| DSM EcoPaXX® Q-X07208 PA410-I-GF30 % Glass Reinforced, Impact Modified |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Minlon® 10B140 NC010 Nylon 66
(Unverified Data**) 40% Mineral Reinforced Polyamide 66Minlon 10B140 NC010 is a 40% mineral reinforced polyamide 66 for injection molding. It has very low warpage.Information provided by DuPont Performance Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Minlon® 10B40HS1 BK061 Nylon 66
(Unverified Data**) 40% Mineral Reinforced Heat Stabilized Polyamide 66 Minlon 10B40HS1 BK061 is a 40% mineral reinforced heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont Pe.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| E-Polymers Tekaster® F615GM , 40% GF/MF Reinforced PET 40% GF/MF Reinforced, Low warpageInformation provided by E-Polymers Co. Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 |
| BASF Petra® 130 FR BK-112 30% Glass Filled PET Petra 130 FR BK-112 is a 30% glass fiber reinforced, black pigmented, flame retardant injection molding compound based on post-consumer and post-industrial recycle polyethylene erephthalate feedstoc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Asia International Enterprise (Hong Kong) 60G3F Nylon 66, 15% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 |
| Polyram PlusTek RA325G4 Nylon 66 for Injection Molding, 20% Glass-Fiber Reinforced, Self-Extinguishing, Halogen Free 20% Glass-fiber reinforced, self-extinguishing halogen free Nylon 66 for injection molding applications.Information provided by Polyram. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | ISO 75-1,-2 |
| Lanxess Durethan® AKV 25 F30 000000 Nylon 66, 25% Glass Fiber PA 66, 25% glass fiber, injection molding, flame retardantInformation provided by LANXESS. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | |
| LATI Kelon® A H CEG/40 PA 66, Glass/Mineral Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati.. |
|||