Borealis Visico™/Ambicat™ ME4425/LE4476 Ambient Curing, Moisture-Crosslinking Polyethylene Compound for Low Voltage Insulation

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Wire/Cable Grade
Manufacturer Borealis
Trade Name Visico™/Ambicat™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Visico™/Ambicat™ ME4425/LE4476 Ambient Curing, Moisture-Crosslinking Polyethylene Compound for Low Voltage Insulation.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Visico LE4423 is a natural, ethylene vinyl silane copolymer that, when combined with the catalyst masterbatch Ambicat LE4476, will undergo an accelerated, moisture-induced crosslinking reaction. This polyethylene compound is highly active and crosslinks rapidly under ambient temperature and humidity conditions, as well as, in a sauna or hot water bath. The combinations of the Visico medium-density polyethylene base material, ME4425, and the patented sulphonic acid catalyst masterbatch, LE4476, provides a highly scorch retardant compound with excellent thermal stability. The higher density of ME4425 exhibits greater chemical resistance, toughness and improved heat deformation resistance. ME4425 contains a permanent scorch retardant additive (SRA) that increases the processing window for moisture crosslinking compound, minimizes the tendency for premature crosslinking in the extruder, head or die and allows the use of highly active crosslinking catalyst like LE4476. LE4476 should be added to ME4425 directly in the extruder hopper by dry blending at a ratio of 5 parts LE4476 to 95 parts ME4425.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
Base ME 4425; ASTM D792
0.933 g/cc
0.0337 lb/in³
Catalyst LE 4476; ASTM D792
Melt Index of Compound 0.70 g/10 min
0.70 g/10 min
ME 4425; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield >= 18.6 MPa
>= 2700 psi
Heat Aging (7 Days at 121°C); ASTM D412
20.7 MPa
3000 psi
ASTM D412
Elongation at Break >= 315 %
>= 315 %
Heat Aging (7 Days at 121°C); ASTM D412
350 %
350 %
ASTM D412
Elongation at Yield >= 50 %
>= 50 %
Hot Creep Test (150°C, 0.20 Mpa); ICEA T-28-562
Tensile Set <= 5.0 %
<= 5.0 %
Hot Creep Test (150°C, 0.20 Mpa); ICEA T-28-562
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 2.3

@Frequency 60 Hz
2.3

@Frequency 60 Hz
ASTM D150
Dielectric Strength >= 21.7 kV/mm
>= 550 kV/in
ASTM D149
Dissipation Factor 0.00050

@Frequency 60 Hz
0.00050

@Frequency 60 Hz
ASTM D150