Carlson Nitronic® 60® Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Carlson
Trade Name Nitronic®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Carlson Nitronic® 60® Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General DescriptionNitronic 60 is an anti-galling and wear resistant austenitic stainless steel. It provides a significantly lower cost alternative to combat wear and galling when compared with cobalt-bearing and high nickel alloys. The uniform corrosion resistance of Nitronic 60 is superior to 304 in most media. Chloride pitting resistance is superior to 316. Room temperature Nitronic 60 also possesses excellent high temperature oxidation resistance and low temperature impact resistance.Due to its grain structure, the galling resistance of Nitronic 60 is superior to that of any other stainless steel. It resists wear, tearing or freeze up of both the primary and contact materials over a wide range of service temperatures. The elevated temperature wear resistance of Nitronic 60 is excellent despite its relatively low hardness when compared with cobalt and nickel-base wear alloys. It also performs well in metal-to-metal wear in nominally inert atmospheres. The cavitation erosion resistance of Nitronic 60 is superior to the austenitic stainless steels as well as high strength duplex (ferritic-austenitic) stainless steels.The general corrosion resistance of Nitronic 60 falls between 304 and 316. However, in a wear system, a galling or seizure failure occurs first followed by dimensional loss due to wear and finally corrosion. Although the general corrosion resistance of Nitronic 60 is not as good as 316, it does offer better chloride pitting, stress corrosion cracking and crevice corrosion resistance.In high temperature service, Nitronic 60 exhibits carburization superior to 316L and 309. Its oxidation resistance is far superior to 304 and 316 and comparable to 309.ApplicationsInfrastructure bridge pin and hanger expansion joints, parking deck expansion joint wear plates.Hydroelectric Power – stems, wicket gate wear ringsOil and Gas Production – pump wear rings, bushings, valve trim, seals, fittings, logging equipment and screens.Food processing and Pharmaceuticals – galling resistant applications in sanitary equipment where lubricants can not be usedChemical and Petrochemical – process valve stems, seats and trim, pump wear rings.Information provided by Carlson
Physical Properties Metric English Comments
Density 7.62 g/cc
0.275 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell <= 241
<= 241
Hardness, Rockwell B <= 100
<= 100
Tensile Strength at Break 631 MPa
91500 psi
Carburized
>= 655 MPa
>= 95000 psi
Tensile Strength, Yield >= 345 MPa

@Strain 0.200 %
>= 50000 psi

@Strain 0.200 %
400 MPa

@Strain 0.200 %
58000 psi

@Strain 0.200 %
Carburized
Elongation at Break 19 %
19 %
Carburized; in 4xD
>= 35 %
>= 35 %
Reduction of Area 21.5 %
21.5 %
Carburized
Modulus of Elasticity 181 GPa
26200 ksi
Taber Abrasion, mg/1000 Cycles 3.2
3.2
vs. Nitronic 32
6.0
6.0
vs. 304
Bend Radius, Minimum 1.5 t
1.5 t
Carburized; 100°
Thermal Properties Metric English Comments
CTE, linear 15.8 µm/m-°C

@Temperature 25.6 - 93.3 °C
8.80 µin/in-°F

@Temperature 78.0 - 200 °F
17.3 µm/m-°C

@Temperature 25.6 - 316 °C
9.60 µin/in-°F

@Temperature 78.0 - 600 °F
18.5 µm/m-°C

@Temperature 25.6 - 649 °C
10.3 µin/in-°F

@Temperature 78.0 - 1200 °F
19.8 µm/m-°C

@Temperature 25.6 - 982 °C
11.0 µin/in-°F

@Temperature 78.0 - 1800 °F
Component Elements Properties Metric English Comments
Carbon, C <= 0.10 %
<= 0.10 %
Chromium, Cr 16 - 18 %
16 - 18 %
Iron, Fe 59.13 - 65.42 %
59.13 - 65.42 %
Manganese, Mn 7.0 - 9.0 %
7.0 - 9.0 %
Nickel, Ni 8.0 - 9.0 %
8.0 - 9.0 %
Nitrogen, N 0.080 - 0.18 %
0.080 - 0.18 %
Phosphorous, P <= 0.060 %
<= 0.060 %
Silicon, Si 3.5 - 4.5 %
3.5 - 4.5 %
Sulfur, S <= 0.030 %
<= 0.030 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000982 ohm-cm
0.0000982 ohm-cm