Category Metal , Nonferrous Metal , Aluminum Alloy , 6000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name DOKIMA®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium DOKIMA® Rolled Plate Aluminum.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOKIMA® rolled plates have moderate strength properties, a very low level of impurities, an excellent corrosion resistance, a very good dimensional stability and high thermal and electrical conductivity. DOKIMA® is recommended for sensitive applications in nuclear, pharmaceutical, food, semi-conductor and telecommunication industries.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.69 g/cc
0.0972 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 100

@Thickness 8.00 - 25.0 mm
 100

@Thickness 0.315 - 0.984 in
100

@Thickness 25.0 - 60.0 mm
 100

@Thickness 0.984 - 2.36 in
100

@Thickness 60.0 - 100 mm
 100

@Thickness 2.36 - 3.94 in
100

@Thickness 100 - 150 mm
 100

@Thickness 3.94 - 5.91 in
Tensile Strength >= 260 MPa

@Thickness 8.00 - 25.0 mm
 >= 37700 psi

@Thickness 0.315 - 0.984 in
 Temper T651
>= 260 MPa

@Thickness 25.0 - 60.0 mm
 >= 37700 psi

@Thickness 0.984 - 2.36 in
 Temper T651
>= 260 MPa

@Thickness 60.0 - 150 mm
 >= 37700 psi

@Thickness 2.36 - 5.91 in
 Temper T651
300 MPa

@Thickness 8.00 - 25.0 mm
 43500 psi

@Thickness 0.315 - 0.984 in
 Typical Strength
300 MPa

@Thickness 25.0 - 60.0 mm
 43500 psi

@Thickness 0.984 - 2.36 in
 Typical Strength
300 MPa

@Thickness 60.0 - 100 mm
 43500 psi

@Thickness 2.36 - 3.94 in
 Typical Strength
300 MPa

@Thickness 100 - 150 mm
 43500 psi

@Thickness 3.94 - 5.91 in
 Typical Strength
Tensile Strength, Yield >= 220 MPa

@Strain 0.200 %,
Thickness 8.00 - 25.0 mm
 >= 31900 psi

@Strain 0.200 %,
Thickness 0.315 - 0.984 in
 Temper T651
>= 220 MPa

@Strain 0.200 %,
Thickness 25.0 - 60.0 mm
 >= 31900 psi

@Strain 0.200 %,
Thickness 0.984 - 2.36 in
 Temper T651
>= 220 MPa

@Strain 0.200 %,
Thickness 60.0 - 150 mm
 >= 31900 psi

@Strain 0.200 %,
Thickness 2.36 - 5.91 in
 Temper T651
260 MPa

@Strain 0.200 %,
Thickness 8.00 - 25.0 mm
 37700 psi

@Strain 0.200 %,
Thickness 0.315 - 0.984 in
 Typical Strength
260 MPa

@Strain 0.200 %,
Thickness 25.0 - 60.0 mm
 37700 psi

@Strain 0.200 %,
Thickness 0.984 - 2.36 in
 Typical Strength
260 MPa

@Strain 0.200 %,
Thickness 60.0 - 100 mm
 37700 psi

@Strain 0.200 %,
Thickness 2.36 - 3.94 in
 Typical Strength
260 MPa

@Strain 0.200 %,
Thickness 100 - 150 mm
 37700 psi

@Strain 0.200 %,
Thickness 3.94 - 5.91 in
 Typical Strength
Elongation at Break >= 5.0 %

@Thickness 60.0 - 150 mm
 >= 5.0 %

@Thickness 2.36 - 5.91 in
 Temper T651
>= 6.0 %

@Thickness 25.0 - 60.0 mm
 >= 6.0 %

@Thickness 0.984 - 2.36 in
 Temper T651
>= 7.0 %

@Thickness 8.00 - 25.0 mm
 >= 7.0 %

@Thickness 0.315 - 0.984 in
 Temper T651
8.0 %

@Thickness 100 - 150 mm
 8.0 %

@Thickness 3.94 - 5.91 in
 Typical Elongation
9.0 %

@Thickness 60.0 - 100 mm
 9.0 %

@Thickness 2.36 - 3.94 in
 Typical Elongation
10 %

@Thickness 8.00 - 25.0 mm
 10 %

@Thickness 0.315 - 0.984 in
 Typical Elongation
10 %

@Thickness 25.0 - 60.0 mm
 10 %

@Thickness 0.984 - 2.36 in
 Typical Elongation
Modulus of Elasticity 68.3 GPa
9910 ksi
Thermal Properties Metric English Comments
CTE, linear 23.4 µm/m-°C

@Temperature 20.0 - 100 °C
 13.0 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 200 W/m-K
1390 BTU-in/hr-ft²-°F
Temper T651
Component Elements Properties Metric English Comments
Aluminum, Al 97.65 - 99.35 %
97.65 - 99.35 %
as balance
Chromium, Cr <= 0.10 %
<= 0.10 %
Copper, Cu <= 0.10 %
<= 0.10 %
Iron, Fe <= 0.35 %
<= 0.35 %
Magnesium, Mg 0.45 - 0.90 %
0.45 - 0.90 %
Manganese, Mn <= 0.10 %
<= 0.10 %
Silicon, Si 0.20 - 0.60 %
0.20 - 0.60 %
Titanium, Ti <= 0.10 %
<= 0.10 %
Zinc, Zn <= 0.10 %
<= 0.10 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000340 ohm-cm
0.00000340 ohm-cm
Temper T651