Covestro Apec® DP9-9340R High-Heat Polycarbonate, Medical with Release  (discontinued **)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, High Heat
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Apec® DP9-9340R High-Heat Polycarbonate, Medical with Release  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
It is the responsibility of the medical device, biological product, or pharmaceutical manufacturer (Manufacturer) to determine the suitability of all component parts and raw materials, including the Bayer Corporation product identified in this electronic database, used in its final product in order to ensure safety and compliance with FDA regulations. This determination must include, as applicable, testing for suitability as an implant device and suitability as to contact with and/or storage of solutions/liquids, including, without limitation, blood, medication, or other bodily fluids. Under no circumstances, however, may the Bayer Corporation product be used in any cosmetic, reconstructive or reproductive implant applications. Nor may any Bayer Corporation resin be used in any other bodily implant applications or any applications involving contact with or storage of human tissue, blood or other bodily fluids for greater than 30 days, based on FDA modified ISO 10993, Part 1 Biological Evaluation of Medical Devices tests. Furthermore, for aromatic grades of Texin TPU resins, longer term uses are not permissible because possible hydrolysis of solid urethane may produce aromatic amines, such as methylene dianiline (MDA). The suitability of a Bayer product in a given end-use environment is dependent upon various conditions including, without limitation, chemical compatibility, temperature, part design, sterilization method, residual stress, or external loads. It is the responsibility of the Manufacturer to evaluate its final product under actual end-use requirements and to adequately advise and warn purchasers and users thereof. Single use medical devices made from Bayer products are not suitable for multiple uses. If the medical device is designed for multiple uses, it is the responsibility of the Manufacturer to determine the appropriate number of permissible uses by evaluating the device under actual sterilization and end-use conditions and to adequately advise and warn purchasers and users thereof. If you have any questions on the regulatory status of any of Bayer Corporation products identified in this electronic database, please contact your local Bayer Corporation representative or the Bayer Corporation Regulatory Affairs Manager in the Health, Environment, and Safety Department in Pittsburgh, Pa. Biocompatibility Information The medical grades of the Bayer Corporation products identified in this electronic database have met the FDA modified ISO 10993, Part 1 Biological Evaluation of Medical Devices tests with human tissue contact time of 30 days or less. ONLY THESE PRODUCTS MAY BE CONSIDERED AS CANDIDATES FOR APPLICATIONS REQUIRING BIOCOMPATIBILITY. No medical grade products will be available for sale until successful completion of testing. Regrind resins must not be used in medical applications requiring biocompatibility. Sterilization Information The sterilization method and the number of sterilization cycles a part made from a Bayer Corporation product identified in this electronic database can withstand will vary depending upon the type and grade of resin, part design, processing parameters, sterilization temperature, and chemical environment. Therefore, the Manufacturer must evaluate each device to deterAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This product was discontinued prior to the separation.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
Water Absorption 0.20 %
0.20 %
24 hour immersion; ASTM D570
Linear Mold Shrinkage 0.0070 - 0.0080 cm/cm
0.0070 - 0.0080 in/in
ASTM D955
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 330 °C
15 g/10 min

@Load 4.76 lb,
Temperature 626 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 83
83
ASTM D785
Hardness, Rockwell R 127
127
ASTM D785
Tensile Strength, Ultimate 64.0 MPa
9280 psi
ASTM D638
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D638
Elongation at Break 80 %
80 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Tensile Modulus 2.20 GPa
319 ksi
ASTM D638
Flexural Yield Strength 86.0 MPa
12500 psi
ASTM D790
Flexural Modulus 2.28 GPa
331 ksi
ASTM D790
Izod Impact, Notched 3.20 J/cm

@Thickness 3.17 mm
5.99 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
NB

@Temperature -40.0 °C
NB

@Temperature -40.0 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 162 °C

@Thickness 3.20 mm
324 °F

@Thickness 0.126 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 150 °C

@Thickness 3.17 mm
302 °F

@Thickness 0.125 in
ASTM D648
Vicat Softening Point 172 °C
342 °F
Rate B; ASTM D1525
Oxygen Index 24 %
24 %
ASTM D2863
Optical Properties Metric English Comments
Refractive Index 1.578
1.578
ASTM D542
Haze 1.0 %

@Thickness 3.17 mm
1.0 %

@Thickness 0.125 in
ASTM D1003
Transmission, Visible 88 %

@Thickness 3.20 mm
88 %

@Thickness 0.126 in
ASTM D1003
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ASTM D257
Dielectric Constant 2.9

@Frequency 60 Hz
2.9

@Frequency 60 Hz
ASTM D150
2.9

@Frequency 1e+6 Hz
2.9

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength >= 16.0 kV/mm

@Thickness 3.17 mm
>= 406 kV/in

@Thickness 0.125 in
ASTM D149
Dissipation Factor 0.0010

@Frequency 60 Hz
0.0010

@Frequency 60 Hz
ASTM D150
0.010

@Frequency 1e+6 Hz
0.010

@Frequency 1e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Melt Temperature 310 - 330 °C
590 - 626 °F