Covestro Bayblend® 2953 Polycarbonate + ABS Blend, Automotive Plating
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Covestro |
| Trade Name | Bayblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Covestro Bayblend® 2953 Polycarbonate + ABS Blend, Automotive Plating.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Spiral Flow | 58.0 cm @Thickness 2.50 mm |
22.8 in @Thickness 0.0984 in |
at 254°C melt temp. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ASTM D638 |
| Flexural Yield Strength | 73.0 MPa | 10600 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 7.50 J/cm @Thickness 3.17 mm |
14.1 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Impact Test | 52.0 J | 38.4 ft-lb | Instrumented Impact, Total Energy; 3.2 mm thick, 7.6 mph, 1.5 in. clamp, 0.5 in. dart; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 77.0 µm/m-°C @Temperature 20.0 °C |
42.8 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C @Thickness 3.17 mm |
205 °F @Thickness 0.125 in |
ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | Rate B; ISO 306 |
| UL RTI, Electrical | 60.0 °C @Thickness 1.57 mm |
140 °F @Thickness 0.0618 in |
|
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness 1.57 mm |
140 °F @Thickness 0.0618 in |
|
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness 1.57 mm |
140 °F @Thickness 0.0618 in |
|
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
|
| HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |