Covestro Bayblend® T90 MF-20* Polycarbonate + ABS, Mineral Filled

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® T90 MF-20* Polycarbonate + ABS, Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Developmental productInjection molding grade20 % mineral filledvery good flowreduced coefficient of thermal dilatationtensile modulus = 5200 MPaVicat/B 120 = 130 °CPreprocessingMax. Water content
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 260 °C
15 g/10 min

@Load 11.0 lb,
Temperature 500 °F
estimated from MVR using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 67.0 MPa
9720 psi
ISO 527-1/-2
Elongation at Yield 3.0 %
3.0 %
ISO 527-1/-2
Tensile Modulus 5.20 GPa
754 ksi
ISO 527-1/-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C
22.2 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 56.0 µm/m-°C
31.1 µin/in-°F
ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 127 °C
261 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 111 °C
232 °F
ISO 75-1/-2
Vicat Softening Point 128 °C
262 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 0.900 mm
HB

@Thickness 0.0354 in
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
IEC 60250
3.3

@Frequency 100 Hz
3.3

@Frequency 100 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243-1
Dissipation Factor 0.0015

@Frequency 100 Hz
0.0015

@Frequency 100 Hz
IEC 60250
0.0032

@Frequency 1.00e+6 Hz
0.0032

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 225 V
225 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
260 °C
500 °F
Injection Molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection Molding; ISO 10724
70.0 - 100 °C
158 - 212 °F
Injection Velocity 240 mm/sec
9.45 in/sec
ISO 294
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
Near East/Africa
South and Central America
Feature Release agent
Form Pellets
Process Injection Molding