Dow DOWLEX™ NG 2085 Linear Low Density Polyethylene, Ethylene-Octene Copolymer

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer	Dow Chemical
Trade Name	DOWLEX™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow DOWLEX™ NG 2085 Linear Low Density Polyethylene, Ethylene-Octene Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Next Generation DOWLEX® NG 2085 resin is an ethylene-octene copolymer offering superior impact and tensile strength for down-gauged consumer liner film applications. It complies with U.S. FDA regulation 21 CFR 177.1520 c 3.2(a) for food contact applications. The regulation should be consulted for complete details.Film properties below based on a film thickness of 25 µm. Data provided by Dow Chemical.

Physical Properties	Metric	English	Comments
Density	0.920 g/cc	0.0332 lb/in³
Thickness	25.0 microns	0.984 mil
Melt Flow	0.95 g/10 min @Load 2.16 kg	0.95 g/10 min @Load 4.76 lb	Melt flow ratio I10/I2 is 8.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	9.90 MPa	1440 psi
Film Tensile Strength at Yield, TD	10.1 MPa	1460 psi
Film Elongation at Break, MD	540 %	540 %
Film Elongation at Break, TD	680 %	680 %
Secant Modulus, MD	0.146 GPa	21.2 ksi	Film value
Secant Modulus, TD	0.1545 GPa	22.41 ksi	Film value
Elmendorf Tear Strength MD	350 g	350 g
Elmendorf Tear Strength TD	665 g	665 g
Elmendorf Tear Strength, MD	14.0 g/micron	356 g/mil
Elmendorf Tear Strength, TD	26.6 g/micron	676 g/mil
Dart Drop	29.0 g/micron	737 g/mil
Film Tensile Strength at Break, MD	58.0 MPa	8410 psi
Film Tensile Strength at Break, TD	46.0 MPa	6670 psi

Processing Properties	Metric	English	Comments
Processing Temperature	224 °C	435 °F	Film extrusion temperature