DuPont Performance Polymers Delrin® 500T BK602 Acetal Homopolymer  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 500T BK602 Acetal Homopolymer  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Delrin® 500T BK602 is a toughened, medium viscosity acetal homopolymer resin with impact resistance similar to Delrin® 100. It can be used in parts requiring noise reduction.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.015 cm/cm

@Thickness 2.00 mm
0.015 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Thickness 2.00 mm
0.015 in/in

@Thickness 0.0787 in
ISO 294-4
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 190 °C
12 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 54.0 MPa

@Temperature 23.0 °C
7830 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 28 %

@Temperature 23.0 °C
28 %

@Temperature 73.4 °F
nominal; ISO 527
45 %

@Temperature 23.0 °C
45 %

@Temperature 73.4 °F
50mm/min; ISO 527
Elongation at Yield 17 %

@Temperature 23.0 °C
17 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 2.20 GPa

@Temperature 23.0 °C
319 ksi

@Temperature 73.4 °F
ISO 527
Flexural Strength 60.0 MPa

@Strain 3.50 %,
Temperature 23.0 °C
8700 psi

@Strain 3.50 %,
Temperature 73.4 °F
ISO 178
Flexural Modulus 2.00 GPa

@Temperature 23.0 °C
290 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature -40.0 °C
4.28 ft-lb/in²

@Temperature -40.0 °F
ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 146 °C
295 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C
169 °F
ISO 75-1/-2
UL RTI, Electrical 105 °C

@Thickness 3.00 mm
221 °F

@Thickness 0.118 in
UL 746B
105 °C

@Thickness 1.50 mm
221 °F

@Thickness 0.0591 in
UL 746B
105 °C

@Thickness 0.750 mm
221 °F

@Thickness 0.0295 in
UL 746B
UL RTI, Mechanical with Impact 85.0 °C

@Thickness 0.750 mm
185 °F

@Thickness 0.0295 in
UL 746B
85.0 °C

@Thickness 1.50 mm
185 °F

@Thickness 0.0591 in
UL 746B
85.0 °C

@Thickness 3.00 mm
185 °F

@Thickness 0.118 in
UL 746B
UL RTI, Mechanical without Impact 85.0 °C

@Thickness 3.00 mm
185 °F

@Thickness 0.118 in
UL 746B
85.0 °C

@Thickness 1.50 mm
185 °F

@Thickness 0.0591 in
UL 746B
85.0 °C

@Thickness 0.750 mm
185 °F

@Thickness 0.0295 in
UL 746B
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
UL94
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
Processing Properties Metric English Comments
Melt Temperature 200 - 210 °C
392 - 410 °F
Injection Molding
205 °C
401 °F
Optimum; Injection Molding
Mold Temperature 50.0 °C
122 °F
optimum; Injection Molding
40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Moisture Content <= 0.050 %
<= 0.050 %
Injection Molding
Descriptive Properties Value Comments
Additive Impact Modifier
Appearance Black Color
Drying Recommended Yes, if moisture content of resin exceeds recommended level
Extrudable - Tubing Yes
Extrudable - Wire and Cable Yes
Features Homopolymer
Impact Modified
Impact Resistance, High
Toughness, Good
Viscosity, Medium
Forms Pellets
Generic Acetal (POM) Homopolymer
Material Status Current
Part Marking Code >POM-I<
ISO 11469
Polymer Family POM
Polymer Type POM Homopolymer
Processing Method Injection Molding
Product Category Toughened Resins
Unreinforced Resins
Region Available - Global Yes
Resin Identification POM-I
ISO 1043
RoHS Compliance Contact Manufacturer
Ultrasonic Weldable Yes
Uses Parts, Engineering