DuPont Performance Polymers Zytel® HTN FE350064 BK544 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Carbon Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN FE350064 BK544 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Carbon Fiber Reinforced Toughened PPA High Performance Polyamide Zytel HTNFE350064 BK544 is a carbon fiber reinforced toughened heat stabilized conductive high performance polyamide resin developed for static dissipative applications. It is also a PPAInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 162 MPa
23500 psi
50%RH; ISO 527-1/-2
168 MPa
24400 psi
DAM; ISO 527-1/-2
Tensile Stress 1.06 MPa

@Strain 0.0300 %,
Temperature 90.0 °C
154 psi

@Strain 0.0300 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
1.26 MPa

@Strain 0.0400 %,
Temperature 40.0 °C
183 psi

@Strain 0.0400 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
1.36 MPa

@Strain 0.0400 %,
Temperature 23.0 °C
197 psi

@Strain 0.0400 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
2.49 MPa

@Strain 0.0400 %,
Temperature 0.000 °C
361 psi

@Strain 0.0400 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
2.61 MPa

@Strain 0.0300 %,
Temperature -20.0 °C
379 psi

@Strain 0.0300 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
2.87 MPa

@Strain 0.0600 %,
Temperature 180 °C
416 psi

@Strain 0.0600 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
2.88 MPa

@Strain 0.0600 %,
Temperature 150 °C
418 psi

@Strain 0.0600 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
3.38 MPa

@Strain 0.0600 %,
Temperature 150 °C
490 psi

@Strain 0.0600 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
4.02 MPa

@Strain 0.0600 %,
Temperature 90.0 °C
583 psi

@Strain 0.0600 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
5.03 MPa

@Strain 0.0500 %,
Temperature 23.0 °C
730 psi

@Strain 0.0500 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
5.19 MPa

@Strain 0.0300 %,
Temperature 40.0 °C
753 psi

@Strain 0.0300 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
5.61 MPa

@Strain 0.0300 %,
Temperature 0.000 °C
814 psi

@Strain 0.0300 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
5.88 MPa

@Strain 0.0300 %,
Temperature -20.0 °C
853 psi

@Strain 0.0300 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
8.78 MPa

@Strain 0.240 %,
Temperature 150 °C
1270 psi

@Strain 0.240 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
8.89 MPa

@Strain 0.230 %,
Temperature 180 °C
1290 psi

@Strain 0.230 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
9.31 MPa

@Strain 0.120 %,
Temperature 90.0 °C
1350 psi

@Strain 0.120 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
9.85 MPa

@Strain 0.150 %,
Temperature 40.0 °C
1430 psi

@Strain 0.150 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
10.05 MPa

@Strain 0.130 %,
Temperature 23.0 °C
1458 psi

@Strain 0.130 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
10.32 MPa

@Strain 0.230 %,
Temperature 150 °C
1497 psi

@Strain 0.230 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
12.48 MPa

@Strain 0.240 %,
Temperature 90.0 °C
1810 psi

@Strain 0.240 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
12.53 MPa

@Strain 0.140 %,
Temperature 0.000 °C
1817 psi

@Strain 0.140 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
12.55 MPa

@Strain 0.130 %,
Temperature -20.0 °C
1820 psi

@Strain 0.130 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
15.1 MPa

@Strain 0.150 %,
Temperature 23.0 °C
2190 psi

@Strain 0.150 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
15.31 MPa

@Strain 0.130 %,
Temperature 40.0 °C
2221 psi

@Strain 0.130 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
16.83 MPa

@Strain 0.120 %,
Temperature 0.000 °C
2441 psi

@Strain 0.120 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
17.3 MPa

@Strain 0.140 %,
Temperature -20.0 °C
2510 psi

@Strain 0.140 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
18.64 MPa

@Strain 0.220 %,
Temperature 23.0 °C
2704 psi

@Strain 0.220 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
22.11 MPa

@Strain 0.220 %,
Temperature 90.0 °C
3207 psi

@Strain 0.220 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
22.45 MPa

@Strain 0.230 %,
Temperature 0.000 °C
3256 psi

@Strain 0.230 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
22.61 MPa

@Strain 0.220 %,
Temperature -20.0 °C
3279 psi

@Strain 0.220 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
23.72 MPa

@Strain 0.240 %,
Temperature 40.0 °C
3440 psi

@Strain 0.240 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
24.79 MPa

@Strain 0.250 %,
Temperature 23.0 °C
3595 psi

@Strain 0.250 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
25.44 MPa

@Strain 0.230 %,
Temperature 40.0 °C
3690 psi

@Strain 0.230 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
27.75 MPa

@Strain 0.220 %,
Temperature 0.000 °C
4025 psi

@Strain 0.220 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
28.29 MPa

@Strain 0.230 %,
Temperature -20.0 °C
4103 psi

@Strain 0.230 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
28.73 MPa

@Strain 1.18 %,
Temperature 180 °C
4167 psi

@Strain 1.18 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
29.42 MPa

@Strain 1.18 %,
Temperature 150 °C
4267 psi

@Strain 1.18 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
34.34 MPa

@Strain 1.10 %,
Temperature 150 °C
4981 psi

@Strain 1.10 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
39.6 MPa

@Strain 2.28 %,
Temperature 180 °C
5740 psi

@Strain 2.28 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
39.78 MPa

@Strain 2.21 %,
Temperature 150 °C
5770 psi

@Strain 2.21 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
42.52 MPa

@Strain 1.12 %,
Temperature 90.0 °C
6167 psi

@Strain 1.12 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
47.22 MPa

@Strain 0.480 %,
Temperature 23.0 °C
6849 psi

@Strain 0.480 %,
Temperature 73.4 °F
DAM; ISO 11403-1 -2
47.86 MPa

@Strain 2.13 %,
Temperature 150 °C
6942 psi

@Strain 2.13 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
50.07 MPa

@Strain 0.490 %,
Temperature 90.0 °C
7262 psi

@Strain 0.490 %,
Temperature 194 °F
DAM; ISO 11403-1 -2
54.17 MPa

@Strain 0.500 %,
Temperature -20.0 °C
7857 psi

@Strain 0.500 %,
Temperature -4.00 °F
DAM; ISO 11403-1 -2
54.75 MPa

@Strain 5.56 %,
Temperature 150 °C
7941 psi

@Strain 5.56 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
54.94 MPa

@Strain 5.81 %,
Temperature 180 °C
7968 psi

@Strain 5.81 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
57.59 MPa

@Strain 7.57 %,
Temperature 150 °C
8353 psi

@Strain 7.57 %,
Temperature 302 °F
50%RH; ISO 11403-1 -2
58.45 MPa

@Strain 2.19 %,
Temperature 90.0 °C
8477 psi

@Strain 2.19 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2
58.53 MPa

@Strain 7.97 %,
Temperature 180 °C
8489 psi

@Strain 7.97 %,
Temperature 356 °F
DAM; ISO 11403-1 -2
60.53 MPa

@Strain 0.590 %,
Temperature 40.0 °C
8779 psi

@Strain 0.590 %,
Temperature 104 °F
DAM; ISO 11403-1 -2
62.25 MPa

@Strain 0.600 %,
Temperature 0.000 °C
9029 psi

@Strain 0.600 %,
Temperature 32.0 °F
DAM; ISO 11403-1 -2
62.29 MPa

@Strain 0.590 %,
Temperature 40.0 °C
9034 psi

@Strain 0.590 %,
Temperature 104 °F
50%RH; ISO 11403-1 -2
65.4 MPa

@Strain 0.550 %,
Temperature 0.000 °C
9490 psi

@Strain 0.550 %,
Temperature 32.0 °F
50%RH; ISO 11403-1 -2
65.88 MPa

@Strain 0.610 %,
Temperature 23.0 °C
9555 psi

@Strain 0.610 %,
Temperature 73.4 °F
50%RH; ISO 11403-1 -2
66.31 MPa

@Strain 5.57 %,
Temperature 150 °C
9617 psi

@Strain 5.57 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
70.02 MPa

@Strain 7.70 %,
Temperature 150 °C
10160 psi

@Strain 7.70 %,
Temperature 302 °F
DAM; ISO 11403-1 -2
72.01 MPa

@Strain 0.600 %,
Temperature -20.0 °C
10440 psi

@Strain 0.600 %,
Temperature -4.00 °F
50%RH; ISO 11403-1 -2
77.35 MPa

@Strain 5.71 %,
Temperature 90.0 °C
11220 psi

@Strain 5.71 %,
Temperature 194 °F
50%RH; ISO 11403-1 -2