EMS-Grivory Grivory® HT2C-3X LF black 9833 PA6T/66-CF30

Category Polymer , Thermoplastic , Nylon , Nylon 6/66
Manufacturer EMS-Grivory (EMS-CHEMIE)
Trade Name Grivory®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EMS-Grivory Grivory® HT2C-3X LF black 9833 PA6T/66-CF30.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product description: Grivory HT2C-3X LF black 9833 is a 30% carbon-fibre reinforced, PTFE modified engineering thermoplastic based on semicrystalline partially aromatic copolyamide. Polymer designation acc. ISO: PA6T/66 Polymer designation acc. ASTM: PPA, Polyphthalamide Grivory HT2C-3X LF black 9833 is especially used in tribological applications. Grivory HT2C-3X LF black 9833 exhibits a high hardness, good crystallinity and a high heat distortion temperature also after moisture absorption. The PTFE (polytetrafluoroethylene) modification reduces the sliding friction after a short initial phase. As each tribological system has its own properties (material combination, temperature, load), the suitability of the product has to be tested for each application under practical conditions.Information provided by EMS Grivory
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Water Absorption 4.3 %
4.3 %
ISO 62
Moisture Absorption 1.50 %
1.50 %
ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
ISO 294-4, 2577
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
0.0030 in/in
ISO 294-4, 2577
Mechanical Properties Metric English Comments
Ball Indentation Hardness 260 MPa
37700 psi
conditioned; ISO 2039-1
290 MPa
42100 psi
dry; ISO 2039-1
Tensile Strength at Break 210 MPa
30500 psi
conditioned; ISO 527-1/-2
240 MPa
34800 psi
dry; ISO 527-1/-2
Elongation at Break 1.5 %
1.5 %
dry; ISO 527-1/-2
2.0 %
2.0 %
conditioned; ISO 527-1/-2
Tensile Modulus 24.0 GPa
3480 ksi
conditioned; ISO 527-1/-2
24.0 GPa
3480 ksi
dry; ISO 527-1/-2
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
dry; ISO 179/1eU
4.00 J/cm²
19.0 ft-lb/in²
conditioned; ISO 179/1eU
4.00 J/cm²

@Temperature 30.0 °C
19.0 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
4.00 J/cm²

@Temperature 30.0 °C
19.0 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
dry; ISO 179/1eA
0.700 J/cm²
3.33 ft-lb/in²
conditioned; ISO 179/1eA
0.500 J/cm²

@Temperature 30.0 °C
2.38 ft-lb/in²

@Temperature 86.0 °F
dry; ISO 179/1eU
0.500 J/cm²

@Temperature 30.0 °C
2.38 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 µm/m-°C
5.56 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C
38.9 µin/in-°F
ISO 11359-1/-2
Melting Point 310 °C
590 °F
10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air 140 °C
284 °F
long term; EMS
240 °C
464 °F
short term; EMS
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ISO 75-1/-2
Deflection Temperature at 8.0 MPa 210 °C
410 °F
ISO 75-1/-2
Flammability, UL94 HB
HB
IEC 60695-11-10
Electrical Properties Metric English Comments
Volume Resistivity 5000 ohm-cm
5000 ohm-cm
dry; IEC 60093
5000 ohm-cm
5000 ohm-cm
conditioned; IEC 60093
Surface Resistance 100 ohm
100 ohm
IEC 60093
Dielectric Strength 3.00 kV/mm
76.2 kV/in
dry; IEC 60243-1
3.00 kV/mm
76.2 kV/in
conditioned; IEC 60243-1
Descriptive Properties Value Comments
Automotive Compressed air systems
Fuel systems
Hydraulic systems
Interior
Powertrain and Chassis
Electricals & Electronics Electrical equipment
Form Granules
Industry & Consumer goods Housewares
Hydraulics & Pneumatics
Mechanical Engineering
Power transmission
Tools & Accessories
Processing Injection Molding
Product Attributes Co Polyamide
Improved alcohol resistance
Improved friction & wear properties
Partially aromatic Polyamide
Special Characteristics Anti-static
Improved heat resistance