Eastman Tenite 285E0V16304 Cellulose Acetate Butyrate, Clear, Trsp

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Butyrate, Molded
Manufacturer Eastman Chemical
Trade Name Tenite
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Tenite 285E0V16304 Cellulose Acetate Butyrate, Clear, Trsp.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications:DisplaysProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite cellulosic plastics are available in natural, clear, selected ambers, or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite Cellulose Acetate Butyrate 285-04 contains an odor mask and has a plasticizer level of 4%.Information provided by Eastman.
Physical Properties Metric English Comments
Specific Gravity 1.205 g/cc
1.205 g/cc
ASTM D792
Water Absorption 1.7 %

@Time 86400 sec
1.7 %

@Time 24.0 hour
Immersion; ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 98
98
ASTM D785
Tensile Strength at Break 52.4 MPa
7600 psi
ASTM D638
Tensile Strength, Yield 43.1 MPa
6250 psi
ASTM D638
Elongation at Break 55 %
55 %
ASTM D638
Flexural Strength 60.0 MPa
8700 psi
ASTM D790
Flexural Modulus 1.793 GPa
260.1 ksi
ASTM D790
Izod Impact, Notched 0.830 J/cm

@Temperature -40.0 °C
1.55 ft-lb/in

@Temperature -40.0 °F
ASTM D256
1.52 J/cm

@Temperature 23.0 °C
2.85 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 110 - 170 µm/m-°C
61.1 - 94.4 µin/in-°F
ASTM D696
Specific Heat Capacity 1.26 - 1.67 J/g-°C
0.301 - 0.399 BTU/lb-°F
DSC
Thermal Conductivity 0.170 - 0.330 W/m-K
1.18 - 2.29 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ASTM D648
Vicat Softening Point 118 °C
244 °F
ASTM D1525
Optical Properties Metric English Comments
Refractive Index 1.46 - 1.49
1.46 - 1.49
n<sub>D</sub>; ASTM D542
Haze <= 8.5 %
<= 8.5 %
ASTM D1003
Transmission, Visible >= 90 %
>= 90 %
ASTM E308
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 - 1.00e+15 ohm-cm
1.00e+13 - 1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.3 - 3.8

@Frequency 1.00e+6 Hz
3.3 - 3.8

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 11.8 - 18.7 kV/mm
300 - 475 kV/in
ASTM D149
Dissipation Factor 0.010 - 0.15

@Frequency 1.00e+6 Hz
0.010 - 0.15

@Frequency 1.00e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Formula Number 285
Odor mask
Plasticizer 4 percent
Soluble Matter Loss 0.1 percent
ASTM D570
Weight Loss on Heating 0.2 percent
ASTM D707, 72 hrs, 80°C