ExxonMobil LL 3301.34 Premium High Strength Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LL 3301.34 Premium High Strength Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LL 3001 resins are hexene copolymer LLDPE film resins. Films produced from this resin have excellent tensile, toughness, and drawability properties. LL 3001 resins are available with blown film additive formulations, with or without antiblock.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.917 g/cc
0.0331 lb/in³
ExxonMobil Method
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Antiblock Level 9000 ppm
9000 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.31 MPa
1350 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 500 %
500 %
ASTM D882
Film Elongation at Break, TD 840 %
840 %
ASTM D882
Puncture Energy 3.05 J
2.25 ft-lb
ExxonMobil
Elmendorf Tear Strength, MD 17.3 g/micron
440 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 29.1 g/micron
740 g/mil
ASTM D1922
Dart Drop 5.51 g/micron
140 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 57.9 MPa
8400 psi
ASTM D882
Film Tensile Strength at Break, TD 48.1 MPa
6980 psi
ASTM D882
1% Secant Modulus, MD 197 MPa
28600 psi
ASTM D882
1% Secant Modulus, TD 238 MPa
34500 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 124 °C
256 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 14.9 %
14.9 %
ASTM D1003
Gloss 49 %
49 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer