Formosa Plastics Formolene® L42022E2 Film (Butene Grade) LLDPE

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film
Manufacturer Formosa Plastics Corporation, USA
Trade Name Formolene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Formosa Plastics Formolene® L42022E2 Film (Butene Grade) LLDPE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Butene Copolymer (Low slip and antiblock)Applications: Thin gauge blown filmThin gauge blown filmMeets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Film properties taken from sample 25 Microns thick, at a 4:1 Blow Up Ratio, 160 X 2.5 mm die, 250 lbs./hrInformation provided by Formosa Plastics Corporation, USA.
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 25.0 microns
0.984 mil
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Condition E; ASTM D1238
Antiblock Level 7000 ppm
7000 ppm
Slip Level 1350 ppm
1350 ppm
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 600 %
600 %
ASTM D882
Film Elongation at Break, TD 800 %
800 %
ASTM D882
Elmendorf Tear Strength, MD 4.33 g/micron
110 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 22.4 g/micron
570 g/mil
ASTM D1922
Dart Drop 2.56 g/micron
65.0 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 26.9 MPa
3900 psi
ASTM D882
Film Tensile Strength at Break, TD 18.6 MPa
2700 psi
ASTM D882
Optical Properties Metric English Comments
Haze 35 %
35 %
ASTM D1003
Gloss 40 %
40 %
45°; ASTM D2457
Descriptive Properties Value Comments
Blow Up Ratio 4 to 1