| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® H802.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat resistance, increased flow.,Property data per ISO test methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Estimated using room temperature density |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | |
| Elongation at Yield | 2.8 % | 2.8 % | |
| Tensile Modulus | 2.70 GPa | 392 ksi | |
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.800 µm/m-°C @Temperature 20.0 °C |
0.444 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | |
| Vicat Softening Point | 109 °C | 228 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
|
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | |
| Dissipation Factor | 0.0060 @Frequency 100 Hz |
0.0060 @Frequency 100 Hz |
|
| 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable 1604-xx07FRD Polyvinyl Chloride, Flexible (PVC, Flexible)
- MV Labs CU420 CuCl2.2H2O Copper(II) chloride dihydrate
- Polymax® Maxelast® F7890 TPE, Fire Retardant
- Gouda Vuurvast CURAS PBK DGM Moldable Refractory Material
- Lubriplate PM 500 White Oil USP Mineral -Based Food Machinery Grade
- SABIC Innovative Plastics Xenoy® XL1339U PC+PET (Europe-Africa-Middle East)
- A. Schulman POLYBLAK™ 4642 Premium Black Color Concentrate, 40% Carbon Black Based In LLDPE
- Diamond Polymers NPP50-0355 High Density Polyethylene Blow Molding/Extrusion Grade
- Clariant ABS4500G10BK ABS, 10% Glass Reinforced
- World Minerals Celite® Super Fine® Super Floss Diatomaceous Earth Antiblock Additive
Copyright © lookpolymers.com All Rights Reserved