Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Ineos ABS NOVODUR® L3FR ABS, Injection Grade  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS NOVODUR® L3FR ABS, Injection Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Injection molding grade, flame retardant, very easy flow. Contains no polyhalogenated diphenyls or diphenyl ethers.Applications: Television and computer housings.Information provided by the manufacturer.Novodur is produced by Styrolution (2014). This grade was discontinued prior to Styrolution's acquisition of the Novodur product line.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Water Absorption 0.30 %
0.30 %
Saturation in water
Water Absorption at Saturation 0.30 %
0.30 %
Melt Flow 48 g/10 min

@Load 10.0 kg,
Temperature 220 °C
48 g/10 min

@Load 22.0 lb,
Temperature 428 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
Elongation at Yield 2.1 %
2.1 %
Tensile Modulus 2.60 GPa
377 ksi
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
0.250 J/cm²

@Temperature -30.0 °C
1.19 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C

@Temperature 20.0 °C
55.6 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Vicat Softening Point 89.0 °C
192 °F
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.20 mm
V-0

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
Dielectric Constant 3.0

@Frequency 1e+6 Hz
3.0

@Frequency 1e+6 Hz
3.1

@Frequency 100 Hz
3.1

@Frequency 100 Hz
Dielectric Strength 24.0 kV/mm
610 kV/in
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
0.0090

@Frequency 1e+6 Hz
0.0090

@Frequency 1e+6 Hz
Comparative Tracking Index 450 V
450 V