Ineos Nova 205 Crystal Polystyrene General Purpose Grade  (discontinued **)

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Transparent Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos Nova 205 Crystal Polystyrene General Purpose Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Easy flow, Good mechanical property balance, Extrusion and Injection MoldingApplications: Sheet and film extrusion, Gloss capping, Blending with HIPS or SBSProperties were determined on injection molded specimens at 23° and 50% RH unless otherwise specified.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets. 
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ISO 1183A
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Melt Flow 13 g/10 min

@Load 5.00 kg,
Temperature 200 °C
13 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ISO 527B
Tensile Strength, Yield 44.0 MPa
6380 psi
ISO 527B
Elongation at Break 3.0 %
3.0 %
ISO 527B
Flexural Modulus 3.10 GPa
450 ksi
ISO 178
Izod Impact, Notched 0.200 J/cm

@Diameter 3.17 mm
0.375 ft-lb/in

@Diameter 0.125 in
bar, 0.010" notch radius; ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
ISO 75
Vicat Softening Point 91.0 °C
196 °F
ISO 306A
Electrical Properties Metric English Comments
Dielectric Constant 2.59

@Frequency 1e+6 Hz
2.59

@Frequency 1e+6 Hz
Dielectric Strength 19.7 kV/mm
500 kV/in
Processing Properties Metric English Comments
Melt Temperature 190 - 274 °C
374 - 525 °F
Mold Temperature 10.0 - 60.0 °C
50.0 - 140 °F