Inno-Comp INNOPOL® CS 1-6140 N 40% Talc-Filled Polypropylene Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler
Manufacturer Inno-Comp Ltd
Trade Name INNOPOL® CS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Inno-Comp INNOPOL® CS 1-6140 N 40% Talc-Filled Polypropylene Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INNOPOL® CS 1-6140 N is a 40% talc-filled polypropylene homopolymer compound /PP-H TD40 (ISO 1043)/.INNOPOL® CS 1-6140 N is developed for producing injection molded components for household equipments. INNOPOL® CS 1-6140 N is high heat and wash-liquor stabilized.All information provided by INNO-COMP.
Physical Properties Metric English Comments
Density 1.22 g/cc

@Temperature 23.0 °C
0.0441 lb/in³

@Temperature 73.4 °F
ISO 1183
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Ash 39 %

@Temperature 600 °C
39 %

@Temperature 1110 °F
ISO 3451-1/A
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 MPa
5080 psi
50 mm/min; ISO 527-1,-2
Elongation at Yield 3.2 %
3.2 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 4.10 GPa
595 ksi
1 mm/min; ISO 527-1,-2
Flexural Modulus 4.20 GPa
609 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 2.20 kJ/m²

@Temperature -20.0 °C
1.05 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
3.50 kJ/m²

@Temperature 23.0 °C
1.67 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 139 °C
282 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
ISO 75-1,-2
Vicat Softening Point 95.0 °C
203 °F
B120; ISO 306
157 °C
315 °F
A120; ISO 306
Descriptive Properties Value Comments
Color Natural