LATI Lapex R PPSU

Category Polymer , Thermoplastic , Polyphenylsulfone (PPSU)
Manufacturer LATI
Trade Name Lapex
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lapex R PPSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfone (PPSU). Unfilled. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm
0.0080 - 0.010 in/in
Linear Mold Shrinkage, Transverse 0.0085 - 0.010 cm/cm
0.0085 - 0.010 in/in
Mechanical Properties Metric English Comments
Elongation at Break >= 100 %

@Temperature 23.0 °C
 >= 100 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
 >= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 2.8 %

@Temperature 150 °C
 2.8 %

@Temperature 302 °F
3.3 %

@Temperature 120 °C
 3.3 %

@Temperature 248 °F
3.8 %

@Temperature 90.0 °C
 3.8 %

@Temperature 194 °F
4.6 %

@Temperature 60.0 °C
 4.6 %

@Temperature 140 °F
5.3 %

@Temperature 23.0 °C
 5.3 %

@Temperature 73.4 °F
Tensile Modulus 2.40 GPa

@Temperature 150 °C
 348 ksi

@Temperature 302 °F
2.50 GPa

@Temperature 120 °C
 363 ksi

@Temperature 248 °F
2.60 GPa

@Temperature 90.0 °C
 377 ksi

@Temperature 194 °F
2.70 GPa

@Temperature 60.0 °C
 392 ksi

@Temperature 140 °F
2.80 GPa

@Temperature 23.0 °C
 406 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 6.00 J/cm²
28.6 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 190 °C
374 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Vicat Softening Point 215 °C

@Load 5.00 kg
 419 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 38 %
38 %
Processing Properties Metric English Comments
Melt Temperature 340 - 380 °C
644 - 716 °F
Mold Temperature 140 - 180 °C
284 - 356 °F
Drying Temperature 140 - 180 °C

@Time 10800 sec
 284 - 356 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa