LG Chemical LUTENE BB0808 LDPE Blown Film Grade
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUTENE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUTENE BB0808 LDPE Blown Film Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: LUTENE BB0808 is mainly intended for the extrusion of blown film with high mechanical property for the manufacture of shrink film and pallet shrink covers. LUTENE BB0808 have the balanced shrink properties and good clarity make suitable for shrink film. (LUTENE BB0808 contains neither slip agent nor antiblock agent.)Main Application: Shrinkage film, Pallet shrink cover, chopping board, All types of industrial packingCAS No. 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ASTM D1505 |
| Water Vapor Transmission | 12.0 g/m²/day | 0.773 g/100 in²/day | |
| Oxygen Transmission Rate | 2000 cc/m²/day | 129 cc/100 in²/day | |
| Nitrogen Transmission | 3500 cc-mm/m²-24hr-atm | 8890 cc-mil/100 in²-24hr-atm | |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50; ASTM D1693 |
| Thickness | 30.0 - 120 microns | 1.18 - 4.72 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 |
| Tear Strength | 275 kN/m | 1570 pli | MD; ASTM D1922 |
| 275 kN/m | 1570 pli | TD; ASTM D1922 | |
| Dart Drop Test | 220 g | 0.485 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 21.6 MPa | 3130 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.6 MPa | 2990 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 110 °C | 230 °F | DSC |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Gloss | 80 % | 80 % | 60°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 - 190 °C | 320 - 374 °F | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 |
Users viewing this material also viewed the following:
- Advanced Elastomer Systems VistaFlex® 911-N Thermoplastic Rubber (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP KFL36 Acetal Copolymer
- Spartech RJ80598 PVC and Alloy Products for Wire and Cable
- Sharadaa Ceramics REFCAST LC90 Low Cement Castables
- Shinkong Synthetic Fibers Shinite® PP4410 PP, Fire Retardant
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N990 (MT) Filler
- Covestro Bayblend® T88 GF-10* Polycarbonate + SAN Glass Filled Impact Grade
- Arkema Group Pebax® MV1074 Polyether Block Amide
- Aclo Accutech Polypropylene Homopolymer HP0339M40L Mica Reinforced
Copyright © lookpolymers.com All Rights Reserved