Lubrizol Advanced Materials PEARLTHANE® 16N87 Thermoplastic Polyurethane Elastomer (discontinued **)
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Advanced Materials PEARLTHANE® 16N87 Thermoplastic Polyurethane Elastomer
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PEARLTHANE® D16N87 is a polyether-based TPU, supplied in form of translucent, colourless or slightly yellowish pellets, offering adequate hardness with superior hydrolysis resistance and improved extrusion processing. Ideally used for applications where excellent microbial resistance and flexibility are required, such as cables and special hoses. It can be easily extruded and injected. PEARLTHANE® D16N87 when extruded, is used for making films, cables, tubing and profiles. When processed by injection moulding, can be used for making technical parts.All information provided by Merquinsa
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 21.6 kg |
10 g/10 min @Load 47.6 lb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 87 | 87 | ASTM D2240 |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D412 |
| Elongation at Break | 590 % | 590 % | ASTM D412 |
| 100% Modulus | 0.006998 GPa | 1.015 ksi | ASTM D412 |
| 300% Modulus | 0.01300 GPa | 1.886 ksi | ASTM D412 |
| Tear Strength | 105 kN/m | 600 pli | ASTM D624 (Die C) |
| Abrasion | 25 | 25 | loss (mm³); DIN 53.516 |
| Compression Set | 24 % @Temperature 22.8 °C, Time 252000 sec |
24 % @Temperature 73.0 °F, Time 70.0 hour |
ASTM D395 |
| 35 % @Temperature 70.0 °C, Time 86400 sec |
35 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 171 - 181 °C | 339 - 357 °F | MQSA 111 |
| Glass Transition Temp, Tg | -48.3 °C | -55.0 °F | DSC, 18ºF/min; DIN 51.007 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 193 °C | 380 °F | |
| Nozzle Temperature | 199 °C | 390 °F | |
| Zone 1 | 204 °C | 400 °F | Compression Zone |
| Zone 2 | 210 °C | 410 °F | Metering Zone |
| Mold Temperature | 35.0 °C | 95.0 °F | |
| Moisture Content | <= 0.050 % | <= 0.050 % | MQSA 44 |
| Injection Pressure | 11.0 MPa | 1600 psi | |
| Hold Pressure | 4.83 MPa @Time 15.0 sec |
700 psi @Time 0.00417 hour |
|
| Cycle Time - Injection | 2.5 sec | 2.5 sec | |
| Cycle Time - Cooling | 38 sec | 38 sec | |
| Screw Speed | 130 rpm | 130 rpm |