LyondellBasell Hifax™ HSBMCB1158LS Thermoplastic Polyolefin Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin
Manufacturer LyondellBasell
Trade Name Hifax™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Hifax™ HSBMCB1158LS Thermoplastic Polyolefin Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Hifax™ HSBMCB1158LS high melt flow, 1,200 MPa flexural modulus, mineral filled thermoplastic elastomeric olefin (TEO) resin has a unique balance of flow, rigidity, low temperature impact resistance, dimensional stability and paintability. It was designed for thin-walled bumper fascia applications that require high paint durability. Features include: high flow, high stiffness, excellent impact resistance, good mold filling capability, good dimensional stability, and very good paint durability. Typical applications include painted automotive thin-walled bumper fascias. Uses: FasciasInformation provided by Basell.
Physical Properties Metric English Comments
Density 0.970 g/cc
0.0350 lb/in³
ISO 1183
Melt Flow 22 g/10 min

@Load 2.16 kg,
Temperature 230 °C
22 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Condition L; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 62
62
ISO 868
Tensile Strength, Yield 18.0 MPa
2610 psi
ISO 527-1, -2
Elongation at Yield 10 %
10 %
ISO 527-1, -2
Flexural Modulus 1.20 GPa
174 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature -40.0 °C
1.90 ft-lb/in²

@Temperature -40.0 °F
ISO 180
4.20 kJ/m²

@Temperature -30.0 °C
2.00 ft-lb/in²

@Temperature -22.0 °F
ISO 180
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
CTE, linear 63.0 µm/m-°C

@Temperature -30.0 - 100 °C
35.0 µin/in-°F

@Temperature -22.0 - 212 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
Unannealed; ISO 75B-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 57.2 °C
135 °F
Unannealed; ISO 75A-1, -2
Shrinkage 0.70 %
0.70 %
Tool, 100x150x3.2 mm; Basell Test Method
1.00 %

@Temperature 121 °C,
Time 3600 sec
1.00 %

@Temperature 250 °F,
Time 1.00 hour
Afterbake, 100x150x3.2 mm; Basell Method