MBA Polymers HDPE 1107 E Post-consumer recycled fractional melt high density polyethylene
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | MBA Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MBA Polymers HDPE 1107 E Post-consumer recycled fractional melt high density polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in standard black.Information provided by MBA Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | MBA Method |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.30 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa @Temperature 23.0 °C |
2900 psi @Temperature 73.4 °F |
ISO 527-2/50 |
| Flexural Modulus | 0.600 GPa @Temperature 23.0 °C |
87.0 ksi @Temperature 73.4 °F |
ISO 178 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding Range |
| 200 °C | 392 °F | Recommended Injection Molding | |
| 190 - 210 °C | 374 - 410 °F | Extrusion Range | |
| 200 °C | 392 °F | Recommended Extrusion | |
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |
| 20.0 °C | 68.0 °F | Recommended | |
| Drying Temperature | 70.0 °C @Time 3600 - 7200 sec |
158 °F @Time 1.00 - 2.00 hour |
|
| Moisture Content | <= 0.10 % | <= 0.10 % |
Users viewing this material also viewed the following:
- Quadrant EPP Ketron® TX PEEK + solid lubricant, extruded (ISO Data)
- LATI LATILUB 88/50-30GRT PEEK Based, 30% Graphite and PTFE Self Lubricating Plastic (Unverified Data**)&l
- MetalTek MTEK 115 Martensitic Stainless Steel
- SABIC Innovative Plastics LNP Thermocomp WX01910L PBT
- Hexcel® HexForce™ 2112 Fiber Glass Fabric
- Zhejiang Juner PP6-1JE PP For Automotive Parts
- CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, UV Stabilized, Heat Stabilized, Dry
- 3M XR8123 Double Coated Paper Tapes
- Atom Adhesives AA-SUPERTHERM 195 Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved