- Multibase Multi-Flex® TPE A 5904 LC BLK
Multibase Multi-Flex® TPE A 5904 LC BLK
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® TPE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® TPE A 5904 LC BLK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Multi-Flex® LC compounds are a new generation elastomers exhibiting improved compression set at elevated temperature. Multi-Flex® TPE compounds are based on Shell's Kraton G technology and feature excellent heat and ozone resistance. LC products cover a wide temperature span from -40°F to 300°F. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 59 | 59 | 10 sec; ASTM D-2240 |
| Tensile Strength, Ultimate | 5.80 MPa | 841 psi | ASTM D638 |
| Elongation at Break | 950 % | 950 % | ASTM D638 |
| 100% Modulus | 0.00230 GPa | 0.334 ksi | ASTM D638 |
| 300% Modulus | 0.00469 GPa | 0.680 ksi | ASTM D638 |
| Tear Strength | 26.3 kN/m | 150 pli | ASTM D624 |
| Compression Set | 17 % | 17 % | for 70 hours at 23°C; ASTM 395 |
| 29 % @Temperature 70.0 °C |
29 % @Temperature 158 °F |
for 70 hours at 70°C; ASTM 395 | |
| 45 % @Temperature 100 °C |
45 % @Temperature 212 °F |
70 hours at 100°C; ASTM 395 |