Plastcom SLOVALEN PH 61 B 70 PP, 70% mineral filling

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVALEN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVALEN PH 61 B 70 PP, 70% mineral filling.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesModified PP for injection moulding with the content of 70% of barium sulphate. Increased density. Decreased shrinkage.Used for production of vertical blind weights. Delivered in natural mode.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 2.04 g/cc
0.0737 lb/in³
Linear Mold Shrinkage 0.0032 cm/cm
0.0032 in/in
Linear Mold Shrinkage, Transverse 0.0046 cm/cm
0.0046 in/in
Melt Flow 10 g/10 min

@Load 0.325 kg,
Temperature 270 °C
10 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 27.0 MPa
3920 psi
Elongation at Break 5.0 %
5.0 %
Tensile Modulus 3.85 GPa
558 ksi
Flexural Strength 85.0 MPa
12300 psi
Flexural Modulus 3.68 GPa
534 ksi
Charpy Impact Unnotched 0.600 J/cm²

@Temperature -20.0 °C
2.86 ft-lb/in²

@Temperature -4.00 °F
2.50 J/cm²

@Temperature 23.0 °C
11.9 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.100 J/cm²

@Temperature -20.0 °C
0.476 ft-lb/in²

@Temperature -4.00 °F
0.150 J/cm²

@Temperature 23.0 °C
0.714 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
Vicat Softening Point 155 °C
311 °F
B
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 50.0 °C
104 - 122 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.20 %
0.20 %
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi