Polimeri Europa Clearflex® CL B0 Very Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Very Low Density Polyethylene (VLDPE)
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® CL B0 Very Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex CL B0 is a linear low density polyethylene, with antioxidants, characterized by a very low density (VLDPE).The resin has a high stretchability and a good cling effect.Main Applications: Clearflex CL B0 is recommended for applications in which soft touch and flexibility are required, for the improvement of impact resistance when used as additive in blend with other polyolefins formulated with or without mineral fillers. Clearflex CL B0 is also used as cling agent in stretch film.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.911 g/cc
0.911 g/cc
ISO 1183
Thickness 8.00 - 50.0 microns
0.315 - 1.97 mil
Recommended
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 7.00 MPa
1020 psi
ISO 527-3
Film Tensile Strength at Yield, TD 7.00 MPa
1020 psi
ISO 527-3
Film Elongation at Break, MD 500 %
500 %
ISO 527-3
Film Elongation at Break, TD 700 %
700 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 3.5665 g/micron
90.589 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 10.19 g/micron
258.8 g/mil
ISO 6383-2
Dart Drop Test 120 g
0.265 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 32.0 MPa
4640 psi
ISO 527-3
Film Tensile Strength at Break, TD 20.0 MPa
2900 psi
ISO 527-3
1% Secant Modulus, MD 80.0 MPa
11600 psi
ISO 527-3
1% Secant Modulus, TD 90.0 MPa
13100 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 118 °C
244 °F
Internal method
Vicat Softening Point 80.0 °C

@Load 1.00 kg
176 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ISO 14782
Gloss 70 %
70 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified