- PolyOne Bergamid™ B70 GK/Mi30 BK Polyamide 6 (Nylon 6)
PolyOne Bergamid™ B70 GK/Mi30 BK Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Bergamid™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Bergamid™ B70 GK/Mi30 BK Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ±0.03; ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.015 cm/cm @Thickness 4.00 mm, Temperature 23.0 °C |
0.010 - 0.015 in/in @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded, Bergmann Method; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 68.0 MPa @Thickness 4.00 mm, Temperature 23.0 °C |
9860 psi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded, 5.0 mm/min; ISO 527 |
| Elongation at Break | >= 4.0 % @Thickness 4.00 mm, Temperature 23.0 °C |
>= 4.0 % @Thickness 0.157 in, Temperature 73.4 °F |
5.0 mm/min; ISO 527 |
| Tensile Modulus | 5.30 GPa @Thickness 4.00 mm, Temperature 23.0 °C |
769 ksi @Thickness 0.157 in, Temperature 73.4 °F |
Injection Molded; ISO 527-2/1 |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
Injection Molded; ISO 179 |
| 3.10 J/cm² @Temperature 23.0 °C |
14.8 ft-lb/in² @Temperature 73.4 °F |
Injection Molded; ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 0.240 J/cm² @Temperature 23.0 °C |
1.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
ALL; Internal Method |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 65.0 - 85.0 °C | 149 - 185 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Features | Good Dimensional Stability | |
| Good Impact Resistance | ||
| Good Stiffness | ||
| Good UV Resistance | ||
| Filler / Reinforcement | Glass BeadMineral, 30% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Processing Method | Injection Molding | |
| Regional Availability | Europe | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Reliance Industries Reclair R35042
- NIZHNEKAMSKNEFTEKHIM PE 6753G (526H7) High Density Polyethylene
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 4.0 PHR MBTS
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with Paraplex G25
- Master Bond EP42HT-2 Epoxy Adhesive Resists Sterilization
- AlphaGary GW 2280 M VW1 LCF Flame Retardant Polyvinyl Chloride
- Beijing Ranger Chem PBT-201-G30 Flame Retarding FR PBT
- Unifrax Fiberfrax® 882-H Ceramic Fiber Paper
- Saint-Gobain CHR® M54 Polyester Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
Copyright © lookpolymers.com All Rights Reserved