PolyOne OnFlex™ BIO 5370A-E0004 Thermoplastic Elastomer (TPE)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name OnFlex™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne OnFlex™ BIO 5370A-E0004 Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
OnFlex™-Bio 5300 series thermoplastic elastomer compounds are soft thermoplastic polyurethane compounds made from renewable natural sources. These compounds contain at least 20% of renewable material as certified according to ASTM-D6866. The OnFlex™-Bio 5300 series compounds are formulated to provide an excellent surface finish, soft-touch haptic, abrasion resistance and mechanical properties.Properties are measured using injection molded plaques.Information provided by PolyOne
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Hardness, Shore A 70
70
ISO 868
Tensile Strength at Break 11.0 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
1600 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
Type 1, 200 mm/min Across Flow; DIN 53504
12.7 MPa

@Thickness 2.00 mm,
Temperature 23.0 °C
1840 psi

@Thickness 0.0787 in,
Temperature 73.4 °F
Type 1, 200 mm/min; Flow; DIN 53504
Tensile Stress 3.30 MPa

@Strain 100 %,
Thickness 2.00 mm
479 psi

@Strain 100 %,
Thickness 0.0787 in
Type 1, 200 mm/min Across Flow; DIN 53504
3.80 MPa

@Strain 100 %,
Thickness 2.00 mm
551 psi

@Strain 100 %,
Thickness 0.0787 in
Type 1, 200 mm/min; Flow; DIN 53504
7.90 MPa

@Strain 300 %,
Thickness 2.00 mm
1150 psi

@Strain 300 %,
Thickness 0.0787 in
Type 1, 200 mm/min Across Flow; DIN 53504
9.20 MPa

@Strain 300 %,
Thickness 2.00 mm
1330 psi

@Strain 300 %,
Thickness 0.0787 in
Type 1, 200 mm/min; Flow; DIN 53504
Elongation at Break 410 %

@Thickness 2.00 mm,
Temperature 23.0 °C
410 %

@Thickness 0.0787 in,
Temperature 73.4 °F
Type 1, 200 mm/min Across Flow; DIN 53504
410 %

@Thickness 2.00 mm,
Temperature 23.0 °C
410 %

@Thickness 0.0787 in,
Temperature 73.4 °F
Type 1, 200 mm/min; Flow; DIN 53504
Tear Strength 43.0 kN/m

@Thickness 2.00 mm,
Temperature 23.0 °C
245 pli

@Thickness 0.0787 in,
Temperature 73.4 °F
Method A, Trouser; Across Flow; ISO 34-1
47.0 kN/m

@Thickness 2.00 mm,
Temperature 23.0 °C
268 pli

@Thickness 0.0787 in,
Temperature 73.4 °F
Method A, Trouser; Flow; ISO 34-1
Abrasion 63
63
[mm³]; DIN 53516
Compression Set 51 %

@Temperature 23.0 °C,
Time 259000 sec
51 %

@Temperature 73.4 °F,
Time 72.0 hour
ISO 815
73 %

@Temperature 70.0 °C,
Time 79200 sec
73 %

@Temperature 158 °F,
Time 22.0 hour
ISO 815
84 %

@Temperature 100 °C,
Time 79200 sec
84 %

@Temperature 212 °F,
Time 22.0 hour
ISO 815
Processing Properties Metric English Comments
Melt Temperature 180 - 220 °C
356 - 428 °F
Mold Temperature 30.0 - 60.0 °C
86.0 - 140 °F
Drying Temperature 100 - 120 °C
212 - 248 °F
Dry Time 1.00 - 2.00 hour
1.00 - 2.00 hour
Descriptive Properties Value Comments
Features Good Abrasion Resistance
Renewable Resource Content
Scratch Resistant
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Injection Rate Fast
Manufacturer / Supplier GLS Thermoplastic Elastomers
Odor rating 3
VDA 270; Method A3
Processing Method Calendering
Extrusion
Injection Molding
Multi Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Uses Automotive Applications
Consumer Applications
General Purpose