SABIC FI1157 Bimodal High Density Polyethylene for Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer SABIC
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC FI1157 Bimodal High Density Polyethylene for Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: FI1157 is a high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, broad molecular weight distribution and high density combine successfully to give excellent extrudability with high film strength and rigidity. The grade is designed specifically to produce thin films with good stiffness.Typical Applications: FI1157 is recommended for blown film extrusion. It can be used for producing grocery sacks, shopping bags, refuse bags, thin films for bag on roll, wrapping film and also for replacement of thin paper products. Films produced with this product can be readily treated and printed to give high quality graphics.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.957 g/cc
0.0346 lb/in³
ISO 1183
Thickness 20.0 microns
0.787 mil
Melt Flow 0.35 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.35 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
11 g/10 min

@Load 21.6 kg,
Temperature 190 °C
11 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 62
62
ISO 868
Film Tensile Strength at Yield, MD 50.0 MPa
7250 psi
ISO 527
Film Tensile Strength at Yield, TD 45.0 MPa
6530 psi
ISO 527
Film Elongation at Break, MD 400 %
400 %
ISO 527
Film Elongation at Break, TD 450 %
450 %
ISO 527
Elmendorf Tear Strength MD 20 g
20 g
ISO 6383-2
Elmendorf Tear Strength TD 45 g
45 g
ISO 6383-2
Elmendorf Tear Strength, MD 1.00 g/micron
25.4 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 2.25 g/micron
57.1 g/mil
ISO 6383-2
Dart Drop 12.0 g/micron
305 g/mil
F50; ASTM D1709
Dart Drop Test 240 g
0.529 lb
F50; ASTM D1709
Thermal Properties Metric English Comments
Vicat Softening Point 75.0 °C
167 °F
ISO 306
Brittleness Temperature <= -80.0 °C
<= -112 °F
ASTM D746
Processing Properties Metric English Comments
Melt Temperature 200 - 225 °C
392 - 437 °F
Blow-up Ratio (BUR) 3.0 - 5.0
3.0 - 5.0