Solvay Specialty Polymers Amodel® A-8930 HS Polyphthalamide (PPA), 30% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-8930 HS Polyphthalamide (PPA), 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® A-8930 HS is a 30% glass-fiber-reinforced, heat-stabilized polyphthalamide (PPA) with a high heat deflection temperature and very high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Heat Resistance; High Stiffness; High Strength; High Temperature Strength; Low Moisture AbsorptionUses: Appliances; Automotive Applications; Automotive Electronics; Connectors; Consumer Applications; Housings; Industrial Applications; Machine/Mechanical Parts; Metal ReplacementInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Additional Properties: Flexural Strain at Break - ISO 178 (23°C): 2.6 %Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ISO 1183
Filler Content 30 %
30 %
Glass Fiber
Water Absorption 0.21 %

@Time 86400 sec
0.21 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0045 cm/cm
0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0089 cm/cm
0.0089 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 194 MPa
28100 psi
ISO 527-2
Elongation at Break 1.8 %
1.8 %
ISO 527-2
Tensile Modulus 12.1 GPa
1750 ksi
ISO 527-2
Flexural Strength 288 MPa
41800 psi
ASTM D790
Flexural Modulus 11.4 GPa
1650 ksi
ISO 178
Izod Impact, Notched (ISO) 8.10 kJ/m²
3.85 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 37.0 kJ/m²

@Temperature -30.0 °C
17.6 ft-lb/in²

@Temperature -22.0 °F
ISO 180
43.0 kJ/m²

@Temperature 23.0 °C
20.5 ft-lb/in²

@Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched 4.60 J/cm²
21.9 ft-lb/in²
Type 1, Edgewise; ISO 179
Charpy Impact, Notched 0.750 J/cm²

@Temperature -30.0 °C
3.57 ft-lb/in²

@Temperature -22.0 °F
Type 1, Edgewise; ISO 179
0.790 J/cm²

@Temperature 23.0 °C
3.76 ft-lb/in²

@Temperature 73.4 °F
Type 1, Edgewise; ISO 179
Thermal Properties Metric English Comments
Melting Point 323 °C
613 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 311 °C
592 °F
HDT B; Unannealed; Flatwise; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 290 °C
554 °F
Unannealed; Flatwise; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 316 - 329 °C
601 - 624 °F
Middle Barrel Temperature 316 - 329 °C
601 - 624 °F
Front Barrel Temperature 324 - 335 °C
615 - 635 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 170 °C
338 °F
Drying Temperature 120 °C

@Time 14400 sec
248 °F

@Time 4.00 hour
Moisture Content 0.030 - 0.060 %
0.030 - 0.060 %
Suggested Max
Descriptive Properties Value Comments
Additive Heat Stabilizer
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black
Form Pellets
Processing Technique Injection Molding